| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.955 |
g/cm3;
|
|
| 熔流率 | 190°C/2.16 kg | ASTM D1238 | 22 |
g/10 min
|
|
| 硬度计硬度 | 支撐 D | ASTM D2240 | 67 | ||
| 抗张强度 |
屈服
|
ASTM D638 | 27.9 |
MPa
|
|
|
断裂
|
ASTM D638 | 14.7 |
MPa
|
||
| 伸长率 | 断裂 | ASTM D638 | 700 | % | |
| 拉伸冲击强度 | ASTM D1822 | 93.2 |
kJ/m2;
|
||
|
热性能 |
脆化温度 | ASTM D746 | -70.0 |
°C
|
|
| 维卡软化温度 | ASTM D1525 | 125 |
°C
|
||
| 熔融温度 | ASTM D1525 | 133 |
°C
|
||