| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.947 |
g/cm3;
|
|
| 熔流率 | 190°C/2.16 kg | ASTM D1238 | 0.75 |
g/10 min
|
|
| 抗环境应力开裂 | ASTM D1693 | 48.0 |
hr
|
||
| 硬度计硬度 | 支撐 D | ASTM D2240 | 65 | ||
| 抗张强度 |
屈服
|
ASTM D638 | 22.6 |
MPa
|
|
|
断裂
|
ASTM D638 | 24.5 |
MPa
|
||
| 伸长率 | 断裂 | ASTM D638 | 600 | % | |
| 拉伸冲击强度 | ASTM D1822 | 255 |
kJ/m2;
|
||
| 热性能 | 脆化温度 | ASTM D746 | -70.0 |
°C
|
|
| 维卡软化温度 | ASTM D1525 | 120 |
°C
|
||
| 熔融温度 | ASTM D1525 | 128 |
°C
|
||
| 电气性能 | 体积电阻率 | ASTM D257 |
1.0E+17
|
ohm·cm
|
|
| 介电常数 | 1 MHz | ASTM D150 | 2.30 | ||
| 耗散因数 | 1 MHz | ASTM D150 |
0.000060
|
||