改性聚苯醚PPE+PA GTX914
性能：通用级，NORYL，改性聚苯醚。
沙伯基础创新塑料(SABIC Innovative Plastics) PPE+PA、GTX4610、GTX673、GTX678、GTX8730、GTX902D、GTX975、GTX989、NX0031、Noryl PPO, Lexan PC, Valox PBT, Ultem PEI, Cycoloy PC/ABS, Xylex PC/PET, Xenoy PC/PBT/PET.
型号：PPE+PA GTX914
Compare
Contact Us
NORYL GTX? Resin
Grades
DeSCRJPTion
GTX4610
PPE+PA, Glass,
Datasheet
Product Data:
Auto Data:
GTX673
PPE+PA, Conductive,
Datasheet
Product Data:
Auto Data:
GTX678
PPE+PA, Flame Retardant, Conductive, Heat Stabilized, Impact Modified, Nonhalogenated,
Datasheet
Product Data:
Auto Data:
GTX8730
PPE+PA, Glass, Conductive,
Datasheet
Product Data:
Auto Data:
GTX902D
NORYL GTX902D is a GTX902E with smaller shaped pellets.
Datasheet
Product Data:
Auto Data:
GTX975
18% mineral filled conductive NORYL GTX.
Datasheet
Product Data:
Auto Data:
GTX989
PPE+PA, Conductive, High Impact,
Datasheet
Product Data:
Auto Data: Auto Specification
NX0031
PPE+PA, conductive with high impact
Datasheet
Product Data:
Auto Data:
NORYL GTX ? Resin NX0031
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
NORYL GTX NX0031 resin is a conductive resin specially designed for electrostatic painting and powder coating applications. This material combines high impact, good flow and conductivity. The material is only available in black and is suitable for injection molding.
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, yld, Type I, 50 mm/min
530
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
480
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
5
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
34
%
ASTM D 638
Tensile Modulus, 5 mm/min
22900
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
800
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
21400
kgf/cm2
ASTM D 790
Tensile Stress, yield, 50 mm/min
50
MPa
ISO 527
Tensile Stress, break, 50 mm/min
48
MPa
ISO 527
Tensile Strain, yield, 50 mm/min
4
%
ISO 527
Tensile Strain, break, 50 mm/min
30
%
ISO 527
Tensile Modulus, 1 mm/min
2000
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
75
MPa
ISO 178
Flexural Modulus, 2 mm/min
1900
MPa
ISO 178
IMPACT
Value
Unit
Standard
Izod Impact, notched, 23°C
22
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
11
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
428
cm-kgf
ASTM D 3763
Izod Impact, notched 80*10*4 +23°C
20
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*4 -30°C
10
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
18
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
10
kJ/m2
ISO 179/1eA
THERMAL
Value
Unit
Standard
Vicat Softening Temp, Rate B/50
175
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed
176
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
136
°C
ASTM D 648
CTE, -40°C to 40°C, flow
1.E-04
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
1.E-04
1/°C
ASTM E 831
CTE, 23°C to 60°C, flow
1.E-04
1/°C
ISO 11359-2
CTE, 23°C to 60°C, xflow
9.E-05
1/°C
ISO 11359-2
Vicat Softening Temp, Rate B/50
175
°C
ISO 306
Vicat Softening Temp, Rate B/120
180
°C
ISO 306
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.09
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
1.3 - 1.6
%
SABIC Method
Melt Flow Rate, 280°C/5.0 kgf
8
g/10 min
ASTM D 1238
Density
1.09
g/cm3
ISO 1183
Water Absorption, (23°C/sat)
4.2
%
ISO 62
Moisture Absorption (23°C / 50% RH)
1.2
%
ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg
8
cm3/10 min
ISO 1133
Source GMD, last updated:2005/01/04
Processing
? Do NOT mix NORYL GTX* resin with other grades of NORYL* resins.
Parameter
Injection Molding
Value
Unit
Drying Temperature
95 - 105
°C
Drying Time
3 - 4
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.07
%
Minimum Moisture Content
0.02
%
Melt Temperature
270 - 295
°C
Nozzle Temperature
270 - 295
°C
Front - Zone 3 Temperature
265 - 295
°C
Middle - Zone 2 Temperature
260 - 295
°C
Rear - Zone 1 Temperature
255 - 295
°C
Mold Temperature
65 - 95
°C
Back Pressure
0.3 - 1.4
MPa
Screw Speed
20 - 100
rpm
Shot to Cylinder Size
30 - 50
%
Vent Depth
0.013 - 0.038
mm