PPO NORYL N300X 阻燃级
PPO NORYL N300X 注塑，未增强，阻燃级，耐高温，高光泽。
PPO 基础创新塑料（美国）NORYL PPX630 物性介绍：30玻纤增强级，良好的刚性，良好的热稳定，良好的韧性。
PPX630 is a 30% glass filled alloy of PP and PPO providing design freedom for applications requiring a wide range of stiffness, toughness and temperature. Generic identification acc. ISO11469: >PP+PPE-I-GF30<
NORYL PPX* PPX630 Resin,Polyphenylene Ether + PS + PP,Glass Fiber Reinforcement,30% Supplied by SABIC Innovative Plastics Europe
PPO 基础创新塑料（美国）NORYL PPX PPX630 原厂英文物性数据表:
PPO 基础创新塑料（美国）NORYL PPX PPX630 注塑成型参数：
干燥温度 65 - 75° C
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, yld, Type I, 5 mm/min
800
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min
800
kgf/cm2
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min
7.7
%
ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span
1320
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
56600
kgf/cm2
ASTM D 790
IMPACT
Value
Unit
Standard
Izod Impact, unnotched, 23°C
84
cm-kgf/cm
ASTM D 4812
Izod Impact, notched, 23°C
16
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
10
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
194
cm-kgf
ASTM D 3763
Instrumented Impact Total Energy, -30°C
208
cm-kgf
ASTM D 3763
THERMAL
Value
Unit
Standard
Vicat Softening Temp, Rate B/50
162
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed
155
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
133
°C
ASTM D 648
CTE, -40°C to 40°C, flow
1.44E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
7.74E-05
1/°C
ASTM E 831
Relative Temp Index, Elec
1
°C
UL 746B
Relative Temp Index, Mech w/impact
1
°C
UL 746B
Relative Temp Index, Mech w/o impact
1
°C
UL 746B
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.19
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.2 - 0.23
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm (5)
0.25 - 0.76
%
SABIC Method
Melt Flow Rate, 260°C/5.0 kgf
2.6
g/10 min
ASTM D 1238
FLAME CHARACTERISTICS
Value
Unit
Standard
UL Recognized, 94HB Flame Class Rating (3)
1.5
mm
UL 94
Parameter
Injection Molding
Value
Unit
Drying Temperature
65 - 75
°C
Drying Time
2 - 4
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.02
%
Melt Temperature
260 - 300
°C
Nozzle Temperature
260 - 300
°C
Front - Zone 3 Temperature
255 - 295
°C
Middle - Zone 2 Temperature
250 - 290
°C
Rear - Zone 1 Temperature
245 - 290
°C
Mold Temperature
40 - 65
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
20 - 100
rpm
Shot to Cylinder Size
30 - 70
%
Vent Depth
0.051 - 0.076
mm
干燥时间 2 - 4小时
干燥时间（累积）8小时
最大水分含量0.02％
熔融温度260 - 300° C
喷嘴温度260 - 300° C
前 - 3区温度255 - 295° C
中东 - 区2温度250 - 290° C
背投 - 区1温度245 - 290° C
模具温度40 - 65° C
背压0.3 - 0.7兆帕
螺杆转速20 - 100RPM
拍摄柱面大小30 - 70％
通风深度0.051 - 0.076毫米