美国奥升德909 PA66加25%玻纤阻燃防火V0
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 |
1.47 g/cm3 | ISO 1183 |
|
收缩率 |
|||
纵向(Flow) |
0.4 % | ISO 294-4 |
23°C, 2.00 mm |
横向(Across Flow) |
1 % | ISO 294-4 |
23°C, 2.00 mm |
吸水率 |
0.7 % | ISO 62 |
24 hr, 23°C |
吸水率 |
1.3 % | ISO 62 |
Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 |
|||
断裂(brk) |
90 Mpa | ISO 527-2 |
Conditioned, 23°C |
断裂(brk) |
132 Mpa | ISO 527-2 |
Dry, 23°C |
拉伸延伸率 |
|||
断裂(brk) |
3 % | ISO 527-2 |
Conditioned, 23°C |
断裂(brk) |
2.2 % | ISO 527-2 |
Dry, 23°C |
弯曲强度 |
|||
- |
140 Mpa | ISO 178 |
Conditioned, 23°C |
- |
193 Mpa | ISO 178 |
Dry, 23°C |
弯曲模量 |
5000 Mpa | ISO 178 |
Conditioned, 23°C |
弯曲模量 |
8300 Mpa | ISO 178 |
Dry, 23°C |
拉伸模量 |
7100 Mpa | ISO 527-2 |
Conditioned, 23°C |
拉伸模量 |
9100 Mpa | ISO 527-2 |
Dry, 23°C |
泊松比 |
0.4 - | ISO 527-2 |
Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) |
|||
-30℃ (-22℉) |
9.5 kJ/m2 | ISO 179/1eA |
Dry |
23℃ (73℉) |
9.4 kJ/m2 | ISO 179/1eA |
Dry |
简支梁无缺口(Charpy Unnotched) |
|||
-30℃ (-22℉) |
35 kJ/m2 | ISO 179/1eU |
Dry |
23℃ (73℉) |
40 kJ/m2 | ISO 179/1eU |
Dry |
悬臂梁缺口(Izod Notched) |
|||
23℃ (73℉) |
9 kJ/m2 | ISO 180 |
Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) |
|||
0.45 Mpa (66 psi)（4.6kg/cm2） |
250 °C | ISO 75-2/B |
Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） |
230 °C | ISO 75-2/A |
Dry, Unannealed |
相对温度指数(RTI) |
|||
冲击w/impact,0.36/0.4mm |
65 °C | UL 746 |
Dry |
冲击w/impact,0.75/0.8mm |
65 °C | UL 746 |
Dry |
冲击w/impact,1.5/1.6 mm |
95 °C | UL 746 |
Dry |
冲击w/impact,3.0/3.2 mm |
95 °C | UL 746 |
Dry |
电气Elec,0.36/0.4mm |
65 °C | UL 746 |
Dry |
电气Elec,0.75/0.8mm |
130 °C | UL 746 |
Dry |
电气Elec,1.5/1.6 mm |
130 °C | UL 746 |
Dry |
电气Elec,3.0/3.2 mm |
130 °C | UL 746 |
Dry |
强度w/o impact,0.36/0.4mm |
65 °C | UL 746 |
Dry |
强度w/o impact,0.75/0.8mm |
110 °C | UL 746 |
Dry |
强度w/o impact,1.5/1.6 mm |
110 °C | UL 746 |
Dry |
强度w/o impact,3.0/3.2 mm |
110 °C | UL 746 |
Dry |
线性膨胀系数(CLTE) |
|||
纵向(Flow) |
20 E-6 cm/cm/℃ | ISO 11359-2 |
Dry, 23 to 55°C, 2.00 mm |
横向(Across Flow) |
100 E-6 cm/cm/℃ | ISO 11359-2 |
Dry, 23 to 55°C, 2.00 mm |
熔融温度(Tm) |
250 °C | ISO 11357-3 |
Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 |
|||
V-0 |
0.4 mm | UL94 |
Dry |
V-0 |
0.75 mm | UL94 |
Dry |
V-0 |
1.5 mm | UL94 |
Dry |
V-0 |
3 mm | UL94 |
Dry |
5VA |
1.5 mm | UL94 |
Dry |
5VA |
3 mm | UL94 |
Dry |
氧指数(LOI) |
32 % | ISO 4589 |
Dry |
灼热丝可燃性指数(GWFI) |
|||
0.4mm |
960 °C | IEC 60695-2-12 |
Dry |
0.71mm |
960 °C | IEC 60695-2-12 |
Dry |
1.5mm |
960 °C | IEC 60695-2-12 |
Dry |
3mm |
960 °C | IEC 60695-2-12 |
Dry |
灼热丝点燃温度(GWIT) |
|||
0.4 mm |
930 °C | IEC 60695-2-13 |
Dry |
0.71mm |
750 °C | IEC 60695-2-13 |
Dry |
1.5mm |
750 °C | IEC 60695-2-13 |
Dry |
3.0mm |
800 °C | IEC 60695-2-13 |
Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) |
|||
- |
250~399 V | IEC 60112 |
Dry, 3.00 mm |
耐电弧性 |
6 PLC | ASTM D495 |
Dry, 3.00 mm |
高电压电弧起痕速率(HVTR) |
3 PLC | UL 746 |
Dry, 3.00 mm |
热线圈起燃性(HWI) |
0 PLC | UL 746 |
Dry, 0.75 mm |
热线圈起燃性(HWI) |
0 PLC | UL 746 |
Dry, 1.50 mm |
高电流弧起燃性(HAI) |
0 PLC | UL 746 |
Dry, 0.75 mm |
高电流弧起燃性(HAI) |
0 PLC | UL 746 |
Dry, 1.50 |
PA66中文名称聚酰胺，俗称尼龙双6，系结晶性热塑性工程塑料。
优点：1、具高张强度；2、耐韧、耐冲击性特优；3、自润性性佳、耐药品性优；4、低温特性佳；5、具自熄性。
用途：
1、电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座、插座、接头、垫圈等；
2、汽车：散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座、滤油器、变速杆等；
3、工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑轮、电动工具等；
4、其他：电动工具、护罩、风叶、齿轮、机床附件、运动器材、玩具制品、扎带等。
注意：
记载数据仅为代表值。
在这里的使用用途例，不对本产品在该用途的适用作出承诺。
有关在这里的用途及应用所涉及的工业所有权或使用条件等，请贵公司自行探讨。
产品使用时的注意事项
1.使用前须将材料进行（烘料）干燥取理。
2.干燥及成型时，会挥发少量挥发性气体鼻，喉咙会造成一定刺激。
在进行这些热处理时，请进行适当的局部通风。
3.粒子如果洒落在地板上，为了避免滑倒，请立即进行清扫。
4.由于可能会发生散落的问题，因此需要进行产品堆积时请留意
898995850