Vydyne美国奥升德R525H PA66加25%玻纤注塑级
| 颜色形状 |
粒状本色 |
|||
| 成型方式 |
注塑 |
|||
| 增强填充 |
25% 玻纤 |
|||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 |
1.32 g/cm3 | ISO 1183 |
Dry |
收缩率 |
|||
纵向(Flow) |
0.4 % | ISO 294-4 |
23°C, 2.00 mm |
横向(Across Flow) |
0.9 % | ISO 294-4 |
23°C, 2.00 mm |
吸水率 |
0.9 % | ISO 62 |
24 hr, 23°C |
吸水率 |
2 % | ISO 62 |
Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 |
|||
断裂(brk) |
117 Mpa | ISO 527-2 |
Conditioned, 23°C |
断裂(brk) |
174 Mpa | ISO 527-2 |
Dry, 23°C |
拉伸延伸率 |
|||
断裂(brk) |
7 % | ISO 527-2 |
Conditioned, 23°C |
断裂(brk) |
3 % | ISO 527-2 |
Dry, 23°C |
弯曲强度 |
|||
- |
150 Mpa | ISO 178 |
Conditioned, 23°C |
- |
250 Mpa | ISO 178 |
Dry, 23°C |
弯曲模量 |
5700 Mpa | ISO 178 |
Conditioned, 23°C |
弯曲模量 |
7700 Mpa | ISO 178 |
Dry, 23°C |
拉伸模量 |
5500 Mpa | ISO 527-2 |
Conditioned, 23°C |
拉伸模量 |
8600 Mpa | ISO 527-2 |
Dry, 23°C |
泊松比 |
0.4 - | ISO 527-2 |
Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) |
|||
-30℃ (-22℉) |
10 kJ/m2 | ISO 179 |
Conditioned |
-30℃ (-22℉) |
10 kJ/m2 | ISO 179 |
Dry |
23℃ (73℉) |
12 kJ/m2 | ISO 179 |
Conditioned |
23℃ (73℉) |
11 kJ/m2 | ISO 179 |
Dry |
简支梁无缺口(Charpy Unnotched) |
|||
-30℃ (-22℉) |
66 kJ/m2 | ISO 179 |
Conditioned |
-30℃ (-22℉) |
55 kJ/m2 | ISO 179 |
Dry |
23℃ (73℉) |
67 kJ/m2 | ISO 179 |
Conditioned |
23℃ (73℉) |
65 kJ/m2 | ISO 179 |
Dry |
悬臂梁缺口(Izod Notched) |
|||
-30℃ (-22℉) |
10 kJ/m2 | ISO 180 |
Conditioned |
-30℃ (-22℉) |
9 kJ/m2 | ISO 180 |
Dry |
23℃ (73℉) |
15 kJ/m2 | ISO 180 |
Conditioned |
23℃ (73℉) |
10 kJ/m2 | ISO 180 |
Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) |
|||
0.45 Mpa (66 psi)（4.6kg/cm2） |
258 °C | ISO 75-2/B |
Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） |
245 °C | ISO 75-2/A |
Dry, Unannealed |
相对温度指数(RTI) |
|||
冲击w/impact,0.75/0.8mm |
120 °C | UL 746 |
Dry |
冲击w/impact,1.5/1.6 mm |
120 °C | UL 746 |
Dry |
冲击w/impact,3.0/3.2 mm |
120 °C | UL 746 |
Dry |
电气Elec,0.75/0.8mm |
140 °C | UL 746 |
Dry |
电气Elec,1.5/1.6 mm |
140 °C | UL 746 |
Dry |
电气Elec,3.0/3.2 mm |
140 °C | UL 746 |
Dry |
强度w/o impact,0.75/0.8mm |
125 °C | UL 746 |
Dry |
强度w/o impact,1.5/1.6 mm |
140 °C | UL 746 |
Dry |
强度w/o impact,3.0/3.2 mm |
140 °C | UL 746 |
Dry |
线性膨胀系数(CLTE) |
|||
纵向(Flow) |
25 E-6 cm/cm/℃ | ISO 11359-2 |
Dry, 23 to 55°C, 2.00 mm |
横向(Across Flow) |
110 E-6 cm/cm/℃ | ISO 11359-2 |
Dry, 23 to 55°C, 2.00 mm |
熔融温度(Tm) |
260 °C | ISO 11357-3 |
Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 |
|||
HB |
0.75 mm | UL94 |
Dry |
HB |
1.5 mm | UL94 |
Dry |
HB |
3 mm | UL94 |
Dry |
灼热丝可燃性指数(GWFI) |
|||
0.75mm |
675 °C | IEC 60695-2-12 |
Dry |
1.5mm |
675 °C | IEC 60695-2-12 |
Dry |
3mm |
675 °C | IEC 60695-2-12 |
Dry |
灼热丝点燃温度(GWIT) |
|||
0.75mm |
700 °C | IEC 60695-2-13 |
Dry |
1.5mm |
700 °C | IEC 60695-2-13 |
Dry |
3.0mm |
700 °C | IEC 60695-2-13 |
Dry |
燃烧速率 |
0 mm/min | ISO 3795 |
Dry, 2.00 |
PA66中文名称聚酰胺，俗称尼龙双6，系结晶性热塑性工程塑料。
优点：1、具高张强度；2、耐韧、耐冲击性特优；3、自润性性佳、耐药品性优；4、低温特性佳；5、具自熄性。
用途：
1、电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座、插座、接头、垫圈等；
2、汽车：散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座、滤油器、变速杆等；
3、工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑轮、电动工具等；
4、其他：电动工具、护罩、风叶、齿轮、机床附件、运动器材、玩具制品、扎带等。
注意：
记载数据仅为代表值。
在这里的使用用途例，不对本产品在该用途的适用作出承诺。
有关在这里的用途及应用所涉及的工业所有权或使用条件等，请贵公司自行探讨。
产品使用时的注意事项
1.使用前须将材料进行（烘料）干燥取理。
2.干燥及成型时，会挥发少量挥发性气体鼻，喉咙会造成一定刺激。
在进行这些热处理时，请进行适当的局部通风。
3.粒子如果洒落在地板上，为了避免滑倒，请立即进行清扫。
4.由于可能会发生散落的问题，因此需要进行产品堆积时请留意
898995850