德国巴斯夫A3X2G5 PA66加25%玻纤阻燃V0
| 产品特性 |
阻燃填充增强 |
|||
| 成型方式 |
注塑 |
|||
| 增强填充 |
25% 玻纤 |
|||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 |
1.34 g/cm3 | ISO 1183 |
|
比重 |
1.34 - | ASTM D792 |
|
熔体体积流动速率(MVR) |
|||
275°C/5 kg |
40 cm3/10 min | ISO 1133 |
|
收缩率 |
|||
- |
0.5 % | Internal |
1/8" bar |
吸水率 |
1.4 % | ASTM D570 |
50% RH |
吸水率 |
6 % | ASTM D570 |
Saturation |
吸水率 |
1.4 % | ISO 62 |
50% RH |
吸水率 |
6 % | ISO 62 |
Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 |
|||
断裂(brk) |
100 Mpa | ISO 527 |
Conditioned,23℃ |
断裂(brk) |
196 Mpa | ISO 527 |
Dry,-40℃ |
断裂(brk) |
140 Mpa | ISO 527 |
Dry,23℃ |
断裂(brk) |
138 Mpa | ASTM D638 |
Dry,23℃ |
拉伸延伸率 |
|||
断裂(brk) |
3 % | ASTM D638 |
Dry,23℃ |
断裂(brk) |
4.5 % | ISO 527 |
Conditioned,23℃ |
断裂(brk) |
3.5 % | ISO 527 |
Dry,-40℃ |
断裂(brk) |
3 % | ISO 527 |
Dry,23℃ |
弯曲模量 |
7100 Mpa | ASTM D790 |
Dry,23℃ |
拉伸模量 |
6000 Mpa | ISO 527 |
Conditioned,23℃ |
拉伸模量 |
8500 Mpa | ISO 527 |
Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) |
|||
-30℃ (-22℉) |
10 kJ/m2 | ISO 179 |
Dry |
23℃ (73℉) |
13 kJ/m2 | ISO 179 |
Dry |
简支梁无缺口(Charpy Unnotched) |
|||
-30℃ (-22℉) |
65 kJ/m2 | ISO 179 |
Conditioned |
-30℃ (-22℉) |
60 kJ/m2 | ISO 179 |
Dry |
23℃ (73℉) |
70 kJ/m2 | ISO 179 |
Conditioned |
23℃ (73℉) |
65 kJ/m2 | ISO 179 |
Dry |
悬臂梁缺口(Izod Notched) |
|||
-40℃ (-40℉) |
64 J/m | ASTM D256 |
Dry |
23℃ (73℉) |
75 J/m | ASTM D256 |
Dry |
23℃ (73℉) |
17 kJ/m2 | ISO 180 |
Conditioned |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) |
|||
0.45 Mpa (66 psi)（4.6kg/cm2） |
250 °C | ASTM D648 |
Dry |
0.45 Mpa (66 psi)（4.6kg/cm2） |
250 °C | ISO 75 |
Dry |
1.8 Mpa (264 psi)（18.6kg/cm2） |
238 °C | ASTM D648 |
Dry |
1.8 Mpa (264 psi)（18.6kg/cm2） |
250 °C | ISO 75 |
Dry |
相对温度指数(RTI) |
|||
冲击w/impact,0.6mm |
115 °C | UL 746B |
|
冲击w/impact,0.81mm |
115 °C | UL 746B |
|
冲击w/impact,1.5/1.6 mm |
115 °C | UL 746B |
|
冲击w/impact,3.0/3.2 mm |
115 °C | UL 746B |
|
电气Elec,0.6mm |
110 °C | UL 746B |
|
电气Elec,0.81mm |
120 °C | UL 746B |
|
电气Elec,1.5/1.6 mm |
120 °C | UL 746B |
|
电气Elec,3.0/3.2 mm |
120 °C | UL 746B |
|
强度w/o impact,0.81mm |
130 °C | UL 746B |
|
强度w/o impact,1.5/1.6 mm |
130 °C | UL 746B |
|
强度w/o impact,3.0/3.2 mm |
130 °C | UL 746B |
|
线性膨胀系数(CLTE) |
|||
纵向(Flow) |
30 E-6/°C | Internal |
Dry |
横向(Across Flow) |
70 E-6/°C | Internal |
Dry |
- |
20 E-6 mm/mm/℃ | ASTM D E831 |
Dry |
熔融温度(Tm) |
260 °C | ASTM D3418 |
Dry |
熔融温度(Tm) |
260 °C | ISO 3146 |
Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 |
|||
HB |
0.6 mm | UL94 |
|
V-0 |
0.81 mm | UL94 |
|
V-0 |
1.5 mm | UL94 |
|
V-0 |
3 mm | UL94 |
|
PA66中文名称聚酰胺，俗称尼龙双6，系结晶性热塑性工程塑料。
优点：1、具高张强度；2、耐韧、耐冲击性特优；3、自润性性佳、耐药品性优；4、低温特性佳；5、具自熄性。
用途：
1、电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座、插座、接头、垫圈等；
2、汽车：散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座、滤油器、变速杆等；
3、工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑轮、电动工具等；
4、其他：电动工具、护罩、风叶、齿轮、机床附件、运动器材、玩具制品、扎带等。
注意：
记载数据仅为代表值。
在这里的使用用途例，不对本产品在该用途的适用作出承诺。
有关在这里的用途及应用所涉及的工业所有权或使用条件等，请贵公司自行探讨。
产品使用时的注意事项
1.使用前须将材料进行（烘料）干燥取理。
2.干燥及成型时，会挥发少量挥发性气体鼻，喉咙会造成一定刺激。
在进行这些热处理时，请进行适当的局部通风。
3.粒子如果洒落在地板上，为了避免滑倒，请立即进行清扫。
4.由于可能会发生散落的问题，因此需要进行产品堆积时请留意