PPO GTX934沙伯基础PPE/PA GTX934
拉伸强度 |
|||
屈服(yld) |
65 Mpa | ASTM D638 |
Type I, 50 mm/min |
屈服(yld) |
65 Mpa | ISO 527 |
50 mm/min |
断裂(brk) |
55 Mpa | ISO 527 |
50 mm/min |
断裂(brk) |
55 Mpa | ASTM D638 |
Type I, 50 mm/min |
拉伸延伸率 |
|||
屈服(yld) |
5 % | ASTM D638 |
Type I, 50 mm/min |
屈服(yld) |
4.5 % | ISO 527 |
50 mm/min |
断裂(brk) |
60 % | ASTM D638 |
Type I, 50 mm/min |
断裂(brk) |
25 % | ISO 527 |
50 mm/min |
弯曲强度 |
|||
屈服(yld) |
95 Mpa | ASTM D790 |
1.3 mm/min, 50 mm span |
屈服(yld) |
90 Mpa | ISO 178 |
2 mm/min |
弯曲模量 |
2350 Mpa | ASTM D790 |
1.3 mm/min, 50 mm span |
弯曲模量 |
2200 Mpa | ISO 178 |
2 mm/min |
拉伸模量 |
2300 Mpa | ASTM D638 |
50 mm/min |
拉伸模量 |
2400 Mpa | ISO 527 |
1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
简支梁缺口(Charpy Notched) |
|||
-30℃ (-22℉) |
10 kJ/m2 | ISO 179/1eA |
V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) |
20 kJ/m2 | ISO 179/1eA |
V-notch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) |
|||
-30℃ (-22℉) |
100 J/m | ASTM D256 |
|
-30℃ (-22℉) |
10 kJ/m2 | ISO 180/1A |
80*10*4 |
23℃ (73℉) |
220 J/m | ASTM D256 |
|
23℃ (73℉) |
20 kJ/m2 | ISO 180/1A |
80*10*4 |