沙伯基础GTX902 注塑PPE/PAGTX902
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 |
1.08 - | ASTM D792 |
|
收缩率 |
|||
纵向(Flow) |
0.9~1.2 % | Internal |
flow, 3.2 mm |
纵向(Flow) |
1.1~1.5 % | Internal |
flow, annealed 130C 1hr |
横向(Across Flow) |
0.8~1.1 % | Internal |
xflow, 3.2 mm |
吸水率 |
0.4 % | ASTM D570 |
24 hours |
吸水率 |
3.6 % | ASTM D570 |
equilibrium, 23C |
磨耗 |
19 mg/1000cy | ASTM D 1044 |
CS-17, 1 kg |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 |
|||
屈服(yld) |
59 Mpa | ASTM D638 |
Type I, 50 mm/min |
断裂(brk) |
56 Mpa | ASTM D638 |
Type I, 50 mm/min |
拉伸延伸率 |
|||
屈服(yld) |
9 % | ASTM D638 |
Type I, 50 mm/min |
断裂(brk) |
52 % | ASTM D638 |
Type I, 50 mm/min |
弯曲强度 |
|||
屈服(yld) |
89 Mpa | ASTM D790 |
2.6 mm/min, 100 mm span |
弯曲模量 |
2240 Mpa | ASTM D790 |
2.6 mm/min, 100 mm span |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) |
|||
-40℃ (-40℉) |
53 J/m | ASTM D256 |
|
-30℃ (-22℉) |
117 J/m | ASTM D256 |
|
23℃ (73℉) |
272 J/m | ASTM D256 |
|
悬臂梁无缺口(Izod Unnotched) |
|||
-40℃ (-40℉) |
3204 J/m | ASTM D 4812 |
|
-30℃ (-22℉) |
3204 J/m | ASTM D 4812 |
|
23℃ (73℉) |
3204 J/m | ASTM D4812 |
|
仪器化落镖冲击能量 |
|||
-40℃ (-40℉)峰值 |
19 J | ASTM D3763 |
|
-30℃ (-22℉)峰值 |
36 J | ASTM D3763 |
|
23℃ (73℉)峰值 |
46 J | ASTM D3763 |
|
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R |
118 R | ASTM D785 |