美国苏威ET-1000HS 高韧性PPAET-1000HS
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 |
1.13 g/cm3 | ISO 1183 |
Dry |
收缩率 |
|||
纵向(Flow) |
1.5 % | ASTM D 955 |
Dry |
横向(Across Flow) |
1.5 % | ASTM D 955 |
Dry |
吸水率 |
0.7 % | ASTM D570 |
24 hr |
磨耗 |
6 mg | ASTM D 1044 |
Dry,1000 Cycles, 1000 g, CS-17 Wheel |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 |
|||
屈服(yld) |
33.8 Mpa | ISO 527-2 |
Dry,100℃ |
屈服(yld) |
70.3 Mpa | ISO 527-2 |
Dry,23℃ |
断裂(brk) |
60 Mpa | ISO 527-2 |
Dry,23℃ |
- |
96.5 Mpa | ASTM D 638 |
Conditioned,-40℃ |
- |
62.7 Mpa | ASTM D 638 |
Conditioned,23℃ |
- |
110 Mpa | ASTM D 638 |
Dry,-40℃ |
- |
68.9 Mpa | ASTM D 638 |
Dry,23℃ |
拉伸延伸率 |
|||
屈服(yld) |
9 % | ASTM D638 |
Conditioned,-40℃ |
屈服(yld) |
6 % | ASTM D638 |
Conditioned,23℃ |
屈服(yld) |
9 % | ASTM D638 |
Dry,-40℃ |
屈服(yld) |
6 % | ASTM D638 |
Dry,23℃ |
屈服(yld) |
4.3 % | ISO 527-2 |
Dry,100℃ |
屈服(yld) |
5 % | ISO 527-2 |
Dry,23℃ |
断裂(brk) |
12 % | ASTM D638 |
Dry,-40℃ |
断裂(brk) |
20 % | ASTM D638 |
Dry,23℃ |
断裂(brk) |
11 % | ISO 527-2 |
Conditioned,-40℃ |
断裂(brk) |
18 % | ISO 527-2 |
Conditioned,23℃ |
断裂(brk) |
95 % | ISO 527-2 |
Dry,100℃ |
断裂(brk) |
7 % | ISO 527-2 |
Dry,23℃ |
弯曲强度 |
|||
- |
85.5 Mpa | ASTM D790 |
Conditioned |
- |
109 Mpa | ASTM D790 |
Dry |
- |
44.1 Mpa | ISO 178 |
Dry,100℃ |
- |
70.3 Mpa | ISO 178 |
Dry,23℃ |
弯曲模量 |
2140 Mpa | ASTM D790 |
Conditioned |
弯曲模量 |
1310 Mpa | ISO 178 |
Dry,100℃ |
弯曲模量 |
1790 Mpa | ISO 178 |
Dry,23℃ |
拉伸模量 |
2410 Mpa | ASTM D638 |
Conditioned |
拉伸模量 |
2280 Mpa | ASTM D638 |
Dry |
拉伸模量 |
2410 Mpa | ASTM D638 |
Dry |
拉伸模量 |
2000 Mpa | ISO 527-2 |
Dry,100℃ |
拉伸模量 |
2410 Mpa | ISO 527-2 |
Dry,23℃ |
剪切强度 |
58.6 Mpa | ASTM D 732 |
Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) |
|||
23℃ (73℉) |
78 kJ/m2 | ISO 179/1eA |
Dry |
简支梁无缺口(Charpy Unnotched) |
|||
23℃ (73℉) |
NB kJ/m2 | ISO 179/1eU |
Dry |
悬臂梁缺口(Izod Notched) |
|||
-40℃ (-40℉) |
110 J/m | ASTM D256 |
Dry |
23℃ (73℉) |
1100 J/m | ASTM D256 |
Conditioned |
23℃ (73℉) |
910 J/m | ASTM D256 |
Dry |
23℃ (73℉) |
73 kJ/m2 | ISO 180/1A |
Dry |
悬臂梁无缺口(Izod Unnotched) |
|||
23℃ (73℉) |
NB kJ/m2 | ISO 180/1U |
Dry |
仪器化落镖冲击能量 |
|||
23℃ (73℉)峰值 |
38 J | ASTM D3763 |
Dry |
23℃ (73℉)总能量 |
54.2 J | ASTM D3763 |
Dry |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R |
120 R | ASTM D785 |
Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) |
|||
1.8 Mpa (264 psi)（18.6kg/cm2） |
120 °C | ASTM D648 |
Annealed |
1.8 Mpa (264 psi)（18.6kg/cm2） |
109 °C | ISO 75-2/A |
Unannealed |
线性膨胀系数(CLTE) |
|||
纵向(Flow) |
77 E-6 cm/cm/℃ | ASTM E831 |
0 to 100℃ |
纵向(Flow) |
140 E-6 cm/cm/℃ | ASTM E831 |
100 to 200℃ |
横向(Across Flow) |
81 E-6 cm/cm/℃ | ASTM E831 |
0 to 100℃ |
横向(Across Flow) |
110 E-6 cm/cm/℃ | ASTM E831 |
100 to 200℃ |
熔融温度(Tm) |
310 °C | ISO 11357-3 |
Dry |
熔融温度(Tm) |
310 °C | ASTM D 570 |
Dry |