PPA美国苏威AS-4133L 玻纤33%增强级 本色 黑色
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 |
1.45 g/cm3 | ISO 1183 |
Dry |
收缩率 |
|||
纵向(Flow) |
0.5 % | ASTM D 955 |
Dry |
横向(Across Flow) |
1 % | ASTM D 955 |
Dry |
吸水率 |
0.29 % | ASTM D570 |
24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 |
|||
断裂(brk) |
172 Mpa | ASTM D638 |
Conditioned |
断裂(brk) |
200 Mpa | ASTM D638 |
Dry |
拉伸延伸率 |
|||
断裂(brk) |
2.2 % | ASTM D638 |
Conditioned |
断裂(brk) |
2.5 % | ASTM D638 |
Dry |
弯曲强度 |
|||
屈服(yld) |
241 Mpa | ASTM D790 |
Conditioned |
屈服(yld) |
290 Mpa | ASTM D790 |
Dry |
弯曲模量 |
11000 Mpa | ASTM D790 |
Conditioned |
弯曲模量 |
11000 Mpa | ASTM D790 |
Dry |
拉伸模量 |
11700 Mpa | ASTM D638 |
Conditioned |
拉伸模量 |
11700 Mpa | ASTM D638 |
Dry |
泊松比 |
0.41 - | ASTM E 132 |
Dry |
剪切强度 |
75.8 Mpa | ASTM D 732 |
Conditioned |
剪切强度 |
90 Mpa | ASTM D 732 |
Dry |
抗压强度 |
172 Mpa | ASTM D 695 |
Conditioned |
抗压强度 |
179 Mpa | ASTM D 695 |
Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) |
|||
- |
69 J/m | ASTM D 256 |
Conditioned |
- |
80 J/m | ASTM D 256 |
Dry |
悬臂梁无缺口(Izod Unnotched) |
|||
- |
960 J/m | ASTM D 256 |
Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) |
|||
0.45 Mpa (66 psi)（4.6kg/cm2） |
320 °C | ASTM D648 |
Dry,Annealed, 3.18 mm |
1.8 Mpa (264 psi)（18.6kg/cm2） |
300 °C | ASTM D648 |
Dry,Annealed, 3.18 mm |
线性膨胀系数(CLTE) |
|||
纵向(Flow) |
22 E-6 cm/cm/℃ | ASTM E831 |
0 to 90℃ |
纵向(Flow) |
14 E-6 cm/cm/℃ | ASTM E831 |
149 to 249℃ |
横向(Across Flow) |
59 E-6 cm/cm/℃ | ASTM E831 |
0 to 90℃ |
横向(Across Flow) |
120 E-6 cm/cm/℃ | ASTM E831 |
149 to 249℃ |
熔融温度(Tm) |
320 °C | ASTM D3418 |
Dry |
熔融温度(Tm) |
320 °C | Internal |
Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 |
|||
HB |
3.2 mm | UL94 |
Dry |