美国苏威A-4145HH 45玻纤PPAA-4145HH
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 |
1.57 g/cm3 | ISO 1183 |
Dry |
收缩率 |
|||
纵向(Flow) |
0.4 % | ASTM D 955 |
Dry |
横向(Across Flow) |
0.8 % | ASTM D 955 |
Dry |
吸水率 |
0.37 % | ASTM D570 |
24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 |
|||
断裂(brk) |
70 Mpa | ISO 527-2 |
Dry,200℃ |
断裂(brk) |
60 Mpa | ISO 527-2 |
Dry,230℃ |
断裂(brk) |
225 Mpa | ISO 527-2 |
Dry,23℃ |
拉伸延伸率 |
|||
断裂(brk) |
6.1 % | ISO 527-2 |
Dry,200℃ |
断裂(brk) |
6.3 % | ISO 527-2 |
Dry,230℃ |
断裂(brk) |
1.8 % | ISO 527-2 |
Dry,23℃ |
弯曲强度 |
|||
- |
325 Mpa | ISO 178 |
Dry,23℃ |
弯曲模量 |
14500 Mpa | ISO 178 |
Dry,23℃ |
拉伸模量 |
16400 Mpa | ISO 527-2 |
Dry |
泊松比 |
0.41 - | ASTM E 132 |
Dry |
剪切强度 |
75.8 Mpa | ASTM D 732 |
Conditioned |
剪切强度 |
89.6 Mpa | ASTM D 732 |
Dry |
抗压强度 |
172 Mpa | ASTM D 695 |
Conditioned |
抗压强度 |
179 Mpa | ASTM D 695 |
Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) |
|||
23℃ (73℉) |
11 kJ/m2 | ISO 179/1eA |
Dry |
简支梁无缺口(Charpy Unnotched) |
|||
23℃ (73℉) |
80 kJ/m2 | ISO 179/1eU |
Dry |
悬臂梁缺口(Izod Notched) |
|||
23℃ (73℉) |
10 kJ/m2 | ISO 180/1A |
Dry |
悬臂梁无缺口(Izod Unnotched) |
|||
23℃ (73℉) |
65 kJ/m2 | ISO 180/1U |
Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) |
|||
1.8 Mpa (264 psi)（18.6kg/cm2） |
297 °C | ISO 75-2/A |
Unannealed |
线性膨胀系数(CLTE) |
|||
纵向(Flow) |
20 E-6 cm/cm/℃ | ASTM E831 |
0 to 100℃ |
纵向(Flow) |
15 E-6 cm/cm/℃ | ASTM E831 |
100 to 200℃ |
横向(Across Flow) |
76 E-6 cm/cm/℃ | ASTM E831 |
0 to 100℃ |
横向(Across Flow) |
120 E-6 cm/cm/℃ | ASTM E831 |
100 to 200℃ |
熔融温度(Tm) |
327 °C | ISO 11357-3 |
Dry |
熔融温度(Tm) |
327 °C | ASTM D 570 |
Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 |
|||
HB |
3.2 mm | UL94 |
Dry |