美国苏威AT-6115HS PPA加15%玻纤增韧级
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
简支梁缺口(Charpy Notched) |
|||
23℃ (73℉) |
11 kJ/m2 | ISO 179/1eA |
Dry |
简支梁无缺口(Charpy Unnotched) |
|||
23℃ (73℉) |
76 kJ/m2 | ISO 179/1eU |
Dry |
悬臂梁缺口(Izod Notched) |
|||
23℃ (73℉) |
12 kJ/m2 | ISO 180/1A |
Dry |
- |
80 J/m | ASTM D 256 |
Conditioned |
- |
91 J/m | ASTM D 256 |
Dry |
悬臂梁无缺口(Izod Unnotched) |
|||
23℃ (73℉) |
55 kJ/m2 | ISO 180/1U |
Dry |
- |
850 J/m | ASTM D 256 |
Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) |
|||
0.45 Mpa (66 psi)（4.6kg/cm2） |
298 °C | ISO 75-2/B |
Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） |
260 °C | ASTM D648 |
Annealed |
1.8 Mpa (264 psi)（18.6kg/cm2） |
251 °C | ISO 75-2/A |
Unannealed |
线性膨胀系数(CLTE) |
|||
纵向(Flow) |
22 E-6 cm/cm/℃ | ASTM E831 |
0 to 100℃ |
纵向(Flow) |
30 E-6 cm/cm/℃ | ASTM E831 |
100 to 200℃ |
横向(Across Flow) |
90 E-6 cm/cm/℃ | ASTM E831 |
0 to 100℃ |
横向(Across Flow) |
120 E-6 cm/cm/℃ | ASTM E831 |
100 to 200℃ |
熔融温度(Tm) |
305 °C | ASTM D3418 |
Dry |
熔融温度(Tm) |
305 °C | ISO 11357-3 |
Dry |