美国苏威A-1133HS PPA加33%玻纤 热稳定
| 颜色形状 |
本色黑色 |
|||
| 成型方式 |
注塑 |
|||
| 增强填充 |
33% 玻纤 |
|||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 |
1.48 g/cm3 | ISO 1183 |
Dry |
收缩率 |
|||
纵向(Flow) |
0.4 % | ASTM D 955 |
Dry |
横向(Across Flow) |
0.8 % | ASTM D 955 |
Dry |
吸水率 |
0.23 % | ASTM D570 |
24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 |
|||
断裂(brk) |
148 Mpa | ISO 527-2 |
Dry,100℃ |
断裂(brk) |
80 Mpa | ISO 527-2 |
Dry,150℃ |
断裂(brk) |
72 Mpa | ISO 527-2 |
Dry,175℃ |
断裂(brk) |
233 Mpa | ISO 527-2 |
Dry,23℃ |
- |
193 Mpa | ASTM D 638 |
Conditioned |
- |
221 Mpa | ASTM D 638 |
Dry |
拉伸延伸率 |
|||
断裂(brk) |
2.1 % | ASTM D638 |
Conditioned |
断裂(brk) |
2.5 % | ASTM D638 |
Dry |
断裂(brk) |
2.9 % | ISO 527-2 |
Dry,100℃ |
断裂(brk) |
8.7 % | ISO 527-2 |
Dry,150℃ |
断裂(brk) |
8.5 % | ISO 527-2 |
Dry,175℃ |
断裂(brk) |
2.5 % | ISO 527-2 |
Dry,23℃ |
弯曲强度 |
|||
- |
254 Mpa | ASTM D790 |
Conditioned |
- |
317 Mpa | ASTM D790 |
Dry |
- |
227 Mpa | ISO 178 |
Dry,100℃ |
- |
93 Mpa | ISO 178 |
Dry,150℃ |
- |
80 Mpa | ISO 178 |
Dry,175℃ |
- |
319 Mpa | ISO 178 |
Dry,23℃ |
弯曲模量 |
11400 Mpa | ASTM D790 |
Conditioned |
弯曲模量 |
11400 Mpa | ASTM D790 |
Dry |
弯曲模量 |
9800 Mpa | ISO 178 |
Dry,100℃ |
弯曲模量 |
4000 Mpa | ISO 178 |
Dry,150℃ |
弯曲模量 |
3600 Mpa | ISO 178 |
Dry,175℃ |
弯曲模量 |
11600 Mpa | ISO 178 |
Dry,23℃ |
拉伸模量 |
13100 Mpa | ASTM D638 |
Conditioned |
拉伸模量 |
13100 Mpa | ASTM D638 |
Dry |
拉伸模量 |
10800 Mpa | ISO 527-2 |
Dry,100℃ |
拉伸模量 |
6700 Mpa | ISO 527-2 |
Dry,150℃ |
拉伸模量 |
4300 Mpa | ISO 527-2 |
Dry,175℃ |
拉伸模量 |
13400 Mpa | ISO 527-2 |
Dry,23℃ |
泊松比 |
0.41 - | ASTM E 132 |
Dry |
剪切强度 |
88.9 Mpa | ASTM D 732 |
Conditioned |
剪切强度 |
101 Mpa | ASTM D 732 |
Dry |
抗压强度 |
185 Mpa | ASTM D 695 |
Dry |