PPA加65%玻纤 美国苏威A-1565HS 尺寸稳定
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 |
1.9 g/cm3 | ISO 1183 |
Dry |
收缩率 |
|||
纵向(Flow) |
0.3 % | ASTM D 955 |
Dry |
横向(Across Flow) |
0.5 % | ASTM D 955 |
Dry |
吸水率 |
0.1 % | ASTM D570 |
24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 |
|||
断裂(brk) |
91.7 Mpa | ISO 527-2 |
Dry,100℃ |
断裂(brk) |
46.2 Mpa | ISO 527-2 |
Dry,150℃ |
断裂(brk) |
32.4 Mpa | ISO 527-2 |
Dry,175℃ |
断裂(brk) |
138 Mpa | ISO 527-2 |
Dry,23℃ |
- |
123 Mpa | ASTM D 638 |
Conditioned |
- |
131 Mpa | ASTM D 638 |
Dry |
拉伸延伸率 |
|||
断裂(brk) |
1.2 % | ASTM D638 |
Conditioned |
断裂(brk) |
1.2 % | ASTM D638 |
Dry |
断裂(brk) |
1.3 % | ISO 527-2 |
Dry,100℃ |
断裂(brk) |
2.4 % | ISO 527-2 |
Dry,150℃ |
断裂(brk) |
1.8 % | ISO 527-2 |
Dry,175℃ |
断裂(brk) |
1 % | ISO 527-2 |
Dry,23℃ |