| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 0.6 | % |
| 吸水率 | 饱和(23℃) | ASTM D-570 | 4.7 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.51 | ||
| 机械性能 | 断裂伸长率 | 23℃,50%RH | ASTM D-638 | 3 | % |
| 断裂伸长率 | 23℃,DAM | ASTM D-638 | 2 | % | |
| 挠曲模量 | 23℃,DAM | ASTM D-790 | 11032 | MPa | |
| 埃佐冲击强度 | 23℃,DAM | ASTM D-256 | 133 | j/m | |
| 拉伸强度 | 23℃,50%RH | ASTM D-638 | 144.7 | MPa | |
| 拉伸强度 | 23℃,DAM | ASTM D-638 | 206.8 | MPa | |
| 挤剪强度 | 23℃,DAM | ASTM D-732 | 93 | MPa | |
| 洛氏硬度M | DAM | ASTM D-785 | M103 | ||
| 挠曲模量 | 23℃,50%RH | ASTM D-790 | 8274 | MPa | |
| 埃佐冲击强度 | 23℃,50%RH | ASTM D-256 | 186 | j/m | |
| 挠曲强度 | 23℃,DAM | ASTM D-790 | 285 | MPa | |
| 电气性能 | 介电强度 | (分步法)DAM | ASTM D-149 | 410 | volts/mil |
| 热性能 | 热畸变温度 | 1.8MPa | ASTM D-648 | 252 | MPa |
| 熔点 | 50%RH | ASTM D-789 | 255 | ℃ | |
| 线性热膨胀系数 | ASTM D-696 | 2.2×10-5 | m/m/℃ | ||
| 熔点 | DAM | ASTM D-789 | 255 | ℃ | |