PA66 FR50 美国杜邦 物性数据
|
|
规格级别：
|
注塑级
|
外观颜色：
|
---
|
|
用途概述：
|
电子/电气应用领域 电气部件 连接器
|
||
|
备注说明：
|
UL94-V0黄卡
|
||
|
性能项目
|
试验条件[状态]
|
测试方法
|
测试数据DAM50%RH
|
数据单位
|
|
|
基本性能
|
吸水率
|
24hr
|
ASTM D-570
|
0.5-
|
%
|
|
物理性能
|
比重
|
---
|
ASTM D-792
|
1.56-
|
---
|
|
模具收缩率
|
3.2mm,flow
|
ASTM D-792
|
0.4-
|
%
|
|
|
机械性能
|
拉伸强度
|
---
|
ASTM D-638
|
169134
|
MPa
|
|
断裂伸长率
|
---
|
ASTM D-638
|
2.54
|
%
|
|
|
弯曲模量
|
---
|
ASTM D-790
|
89606900
|
MPa
|
|
|
弯曲强度
|
---
|
ASTM D-790
|
240-
|
MPa
|
|
|
IZOD缺口冲击强度
|
---
|
ASTM D-256
|
100105
|
J/m
|
|
|
电气性能
|
损耗因数
|
10Hz
|
ASTM D-150
|
0.0140.041
|
---
|
|
介电常数
|
10Hz
|
ASTM D-150
|
3.53.8
|
---
|
|
|
损耗因数
|
10Hz
|
ASTM D-150
|
0.541
|
---
|
|
|
表面电阻率
|
---
|
ASTM D-257
|
1010
|
Ω
|
|
|
体积电阻率
|
---
|
ASTM D-257
|
1010
|
Ω.cm
|
|
|
介电强度
|
3.2mm
|
ASTM D-149
|
17.215.6
|
kv/mm
|
|
|
介电常数
|
10Hz
|
ASTM D-150
|
3.65.1
|
---
|
|
|
热 性 能
|
热变形温度
|
0.45MPa
|
ASMT D-648
|
257-
|
℃
|
|
热变形温度
|
1.80MPa
|
ASTM D-648
|
235-
|
MPa
|
|
|
熔点
|
---
|
ASTM D-3418
|
262-
|
℃
|
|
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
相比耐漏电起痕指数(CTI)
|
PLC 2
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
|
|
|
|
0.350 mm
|
V-0
|
|
UL 94,IEC 60695-11-10, -20 |
|
0.750 mm
|
V-0
|
|
UL 94,IEC 60695-11-10, -20 |
|
1.50 mm
|
5VA
|
|
UL 94 |
|
3.00 mm
|
5VA
|
|
UL 94 |
|
1.50 mm
|
|
|
IEC 60695-11-10, -20 |
|
3.00 mm
|
V-0
|
|
IEC 60695-11-10, -20 |
|
灼热丝易燃指数
|
|
|
IEC 60695-2-12 |
|
0.750 mm
|
960
|
°C
|
|
|
1.50 mm
|
960
|
°C
|
|
|
3.00 mm
|
960
|
°C
|
|
|
热灯丝点火温度
|
|
|
IEC 60695-2-13 |
|
0.750 mm
|
900
|
°C
|
|
|
1.50 mm
|
900
|
°C
|
|
|
3.00 mm
|
930
|
°C
|
|
| 注射成型参数 |
额定值
|
单位制
|
|
|
干燥温度
|
80.0
|
°C
|
|
|
干燥时间
|
2.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
< 0.20
|
%
|
|
|
加工（熔体）温度
|
270 到 290
|
°C
|
|
|
Melt Temperature, Optimum
|
280
|
°C
|
|
|
模具温度
|
70.0 到 120
|
°C
|
|
|
Mold Temperature, Optimum
|
100
|
°C
|
|
898995850