HIPS(改苯#高抗冲聚苯乙烯/改性聚苯乙烯)/HI-450/韩国锦湖
原料描述部分
|
规格级别 |
其它 其它 其它 |
外观颜色 |
|
|
该料用途 |
|
||
|
备注说明 |
良好的耐磨性 |
||
原料技术数据
|
性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
|
|
基本性能 |
熔体流动速率 |
200℃/5kg |
ASTM D-1238 |
4.0 |
g/10min |
|
模具收缩率 |
Flow |
ASTM D-955 |
0.30-0.60 |
% |
|
|
吸水率 |
24hr |
ASTM D-570 |
0.050 |
% |
|
|
物理性能 |
比重 |
|
ASTM D-792 |
1.04 |
g/cm3 |
|
机械性能 |
拉伸屈服强度 |
|
ASTM D-638 |
40.1 |
MPa |
|
拉伸屈服伸长率 |
|
ASTM D-638 |
45 |
% |
|
|
弯曲模量 |
|
ASTM D-790 |
2250 |
MPa |
|
|
弯曲屈服强度 |
|
ASTM D-790 |
43.1 |
MPa |
|
|
IZOD缺口冲击强度 |
3.18mm |
ASTM D-256 |
89.1 |
J/m |
|
|
洛氏硬度 |
|
ASTM D-785 |
80 |
L scale |
|
|
电气性能 |
体积电阻率 |
|
ASTM D-257 |
1.0E+16 |
ohm.cm |
|
介电强度 |
|
ASTM D-149 |
17.7 |
KV/mm |
|
|
介电常数 |
1E+6Hz |
ASTM D-150 |
2.700 |
|
|
|
热性能 |
热变形温度 |
1.80MPa，未退火 |
ASTM D-648 |
82.2 |
℃ |
|
维卡软化温度 |
|
ASTM D-1525 |
101 |
℃ |
|
|
燃烧性 |
1.59mm |
UL 94 |
HB |
|
|
|
燃烧性 |
3.18mm |
UL 94 |
HB |
|
|
|
燃烧性 |
6.35mm |
UL 94 |
HB |
|
|
|
RTI Str |
1.59mm |
UL 746 |
50.0 |
℃ |
|
|
RTI Str |
3.18mm |
UL 746 |
50.0 |
℃ |
|