| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | 23℃ | ASTM D-792 | 1.04 | g/cm3 |
| 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 20 | g/10min | |
| 熔体流动速率 | 200℃×5kg | ASTM D-1238 | 2.2 | g/10min | |
| 物理性能 | 阻燃性 | UL 94 | HB | CLASS | |
| 光泽度 | 60° | ASTM D-523 | 88 | ||
| 机械性能 | IZOD冲击强度 | 23℃，6.4mm | ASTM D-256 | 15.0 | kg.cm/cm |
| 伸长率 | 50mm/min | ASTM D-638 | 22 | % | |
| 拉伸强度 | 50mm/min | ASTM D-638 | 550 | Kg/cm2 | |
| 洛氏硬度 | R scale | ASTM D-785 | 105 | R | |
| 弯曲模量 | 3mm/min | ASTM D-790 | 23000 | Kg/cm2 | |
| 弯曲强度 | 3mm/min | ASTM D-790 | 660 | Kg/cm2 | |
| IZOD冲击强度 | 23℃，3.2mm | ASTM D-256 | 13.0 | kg.cm/cm | |
| 加工性能 | 成型收缩率 | ASTM D-955 | 0.4～0.7 | % | |
| 热性能 | 热变形温度 | 1/4″(18.6kg/ cm2) | ASTM D-648 | 90(194) | ℃(℉) |