性能：阻燃级，阻燃PC/ABS 耐热级。
CYCOLOY? Resin C6200 |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
680
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
50
|
%
|
ASTM D 638
|
|
|
Flexural Stress, yld, 2.6 mm/min, 100 mm span
|
1050
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 2.6 mm/min, 100 mm span
|
27400
|
kgf/cm2
|
ASTM D 790
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
54
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Energy @ peak, 23°C
|
622
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Energy @ peak, -30
|
553
|
cm-kgf
|
ASTM D 3763
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
87
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
90
|
°C
|
ASTM D 648
|
|
|
Relative Temp Index, Elec
|
85
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
85
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
85
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.18
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.4 - 0.6
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.4 - 0.6
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/2.16 kgf
|
14.5
|
g/10 min
|
ASTM D 1238
|
|
|
Spiral Flow,260°C,10 ips,3.175 X 1524 mm
|
685.8
|
mm
|
-
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Arc Resistance, Tungsten {PLC}
|
6
|
PLC Code
|
ASTM D 495
|
|
|
Hot Wire Ignition {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
|
High Voltage Arc Track Rate {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
|
High Ampere Arc Ign, surface {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
|
Comparative Tracking Index (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
|
Volume Resistivity
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
|
Surface Resistivity, ROA
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
|
Dielectric Strength, in oil, 0.8 mm
|
35
|
kV/mm
|
IEC 60243-1
|
|
|
Dielectric Strength, in oil, 1.6 mm
|
25
|
kV/mm
|
IEC 60243-1
|
|
|
Dielectric Strength, in oil, 3.2 mm
|
17
|
kV/mm
|
IEC 60243-1
|
|
|
Relative Permittivity, 1 MHz
|
2.7
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 50/60 Hz
|
0.004
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 1 MHz
|
0.008
|
-
|
IEC 60250
|
|
|
Relative Permittivity, 50/60 Hz
|
2.8
|
-
|
IEC 60250
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94HB Flame Class Rating (3)
|
0.71
|
mm
|
UL 94
|
|
|
UL Recognized, 94V-1 Flame Class Rating (3)
|
1.21
|
mm
|
UL 94
|
|
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
1.47
|
mm
|
UL 94
|
|
|
UL Recognized, 94-5VA Rating (3)
|
3.4
|
mm
|
UL 94
|
|
|
UL Recognized, 94-5VB Rating (3)
|
2
|
mm
|
UL 94
|
|
|
Source GMD, last updated:2000/01/05
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
80 - 90
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.04
|
%
|
|
Melt Temperature
|
245 - 275
|
°C
|
|
Nozzle Temperature
|
245 - 275
|
°C
|
|
Front - Zone 3 Temperature
|
245 - 275
|
°C
|
|
Middle - Zone 2 Temperature
|
220 - 275
|
°C
|
|
Rear - Zone 1 Temperature
|
220 - 255
|
°C
|
|
Mold Temperature
|
60 - 80
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
40 - 70
|
rpm
|
|
Shot to Cylinder Size
|
30 - 80
|
%
|
|
Vent Depth
|
0.038 - 0.076
|
mm
|