性能：通用级，10% GR，Cycoloy PC/ABS，高流量，高耐热性，高强度，高刚度。
CYCOLOY? Resin C4210HF |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 5 mm/min
|
860
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
860
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
3
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
3
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
49900
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, brk, 1.3 mm/min, 50 mm span
|
1420
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
43800
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 5 mm/min
|
90
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 5 mm/min
|
90
|
MPa
|
ISO 527
|
|
|
Tensile Strain, break, 5 mm/min
|
3.2
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
4700
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
125
|
MPa
|
ISO 178
|
|
|
Flexural Stress, break, 2 mm/min
|
135
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
4250
|
MPa
|
ISO 178
|
|
|
Hardness, H358/30
|
116
|
MPa
|
ISO 2039-1
|
|
|
Hardness, Rockwell R
|
121
|
-
|
ISO 2039-2
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, unnotched, 23°C
|
48
|
cm-kgf/cm
|
ASTM D 4812
|
|
|
Izod Impact, unnotched, -30°C
|
48
|
cm-kgf/cm
|
ASTM D 4812
|
|
|
Izod Impact, notched, 23°C
|
7
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
6
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
152
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Total Energy, -30°C
|
81
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, unnotched 80*10*4 +23°C
|
30
|
kJ/m2
|
ISO 180/1U
|
|
|
Izod Impact, notched 80*10*4 +23°C
|
8
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*4 -30°C
|
6
|
kJ/m2
|
ISO 180/1A
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
134
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
126
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
128
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
4.E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
7.5E-05
|
1/°C
|
ASTM E 831
|
|
|
Thermal Conductivity
|
0.2
|
W/m-°C
|
ISO 8302
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.22
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.3 - 0.5
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.3 - 0.5
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/5.0 kgf
|
37
|
g/10 min
|
ASTM D 1238
|
|
898995850