性能：通用级，非溴化阻燃PC/ABS。
CYCOLOY? Resin C2950 |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced flow and impact plus improved heat resistance intended for various applications.
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
630
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
40
|
%
|
ASTM D 638
|
|
|
Flexural Stress, yld, 2.6 mm/min, 100 mm span
|
1040
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 2.6 mm/min, 100 mm span
|
27000
|
kgf/cm2
|
ASTM D 790
|
|
|
Hardness, Rockwell R
|
123
|
-
|
ASTM D 785
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
54
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
16
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
622
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Total Energy, -30°C
|
553
|
cm-kgf
|
ASTM D 3763
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
112
|
°C
|
ASTM D 1525
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
90
|
°C
|
ASTM D 648
|
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
104
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
95
|
°C
|
ASTM D 648
|
|
|
CTE, -30°C to 30°C, flow
|
7.2E-05
|
1/°C
|
ASTM D 696
|
|
|
CTE, -30°C to 30°C, xflow
|
7.2E-05
|
1/°C
|
ASTM D 696
|
|
|
Thermal Conductivity
|
0.2
|
W/m-°C
|
ASTM C 177
|
|
|
Relative Temp Index, Elec
|
85
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
85
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
85
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.18
|
-
|
ASTM D 792
|
|
|
Specific Gravity, color
|
1.22
|
-
|
ASTM D 792
|
|
|
Water Absorption, 24 hours
|
0.1
|
%
|
ASTM D 570
|
|
|
Water Absorption, equilibrium, 23C
|
0.4
|
%
|
ASTM D 570
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.4 - 0.6
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.4 - 0.6
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/2.16 kgf
|
10
|
g/10 min
|
ASTM D 1238
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Volume Resistivity
|
1.E+17
|
Ohm-cm
|
ASTM D 257
|
|
|
Surface Resistivity
|
>1.E+16
|
Ohm
|
ASTM D 257
|
|
|
Dielectric Strength, in oil, 3.2 mm
|
19.4
|
kV/mm
|
ASTM D 149
|
|
|
Relative Permittivity, 50/60 Hz
|
3
|
-
|
ASTM D 150
|
|
|
Relative Permittivity, 100 Hz
|
3
|
-
|
ASTM D 150
|
|
|
Dissipation Factor, 50/60 Hz
|
0.005
|
-
|
ASTM D 150
|
|
|
Dissipation Factor, 100 Hz
|
0.0049
|
-
|
ASTM D 150
|
|
|
Arc Resistance, Tungsten {PLC}
|
6
|
PLC Code
|
ASTM D 495
|
|
|
Hot Wire Ignition {PLC)
|
1
|
PLC Code
|
UL 746A
|
|
|
High Voltage Arc Track Rate {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
|
High Ampere Arc Ign, surface {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
|
Comparative Tracking Index (UL) {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
1.49
|
mm
|
UL 94
|
|
|
UL Recognized, 94-5VB Rating (3)
|
2.48
|
mm
|
UL 94
|
|
|
Oxygen Index (LOI)
|
32
|
%
|
ASTM D 2863
|
|
|
Source GMD, last updated:2000/01/05
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
80 - 90
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.04
|
%
|
|
Melt Temperature
|
245 - 275
|
°C
|
|
Nozzle Temperature
|
245 - 275
|
°C
|
|
Front - Zone 3 Temperature
|
245 - 275
|
°C
|
|
Middle - Zone 2 Temperature
|
220 - 275
|
°C
|
|
Rear - Zone 1 Temperature
|
220 - 255
|
°C
|
|
Mold Temperature
|
60 - 80
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
40 - 70
|
rpm
|
|
Shot to Cylinder Size
|
30 - 80
|
%
|
|
Vent Depth
|
0.038 - 0.076
|
mm
|
898995850