性能：阻燃级，非溴化阻燃Cycoloy PC/ABS。耐磨，阻燃化合物。
CYCOLOY? Resin C2805 |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
LNP* Lubricomp* Cycoloy* C2805 compound is a PTFE reinforced PC+ABS, wear resistant, flame retardant compound for moving components in business equipment. Medium heat performance
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
630
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
520
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
110
|
%
|
ASTM D 638
|
|
|
Flexural Stress, yld, 2.6 mm/min, 100 mm span
|
970
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 2.6 mm/min, 100 mm span
|
27700
|
kgf/cm2
|
ASTM D 790
|
|
|
K-factor xE-10, PV=2000 psi-fpm vs Steel
|
430
|
-
|
SABIC Method
|
|
|
Coefficient of Friction on steel, Static
|
0.16
|
-
|
ASTM D 1894
|
|
|
Coefficient of Friction on steel,Kinetic
|
0.21
|
-
|
ASTM D 1894
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
13
|
cm-kgf/cm
|
ASTM D 256
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
82
|
°C
|
ASTM D 648
|
|
|
Relative Temp Index, Elec
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
60
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.22
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.4 - 0.5
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.3 - 0.5
|
%
|
SABIC Method
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Hot Wire Ignition {PLC)
|
3
|
PLC Code
|
UL 746A
|
|
|
High Ampere Arc Ign, surface {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
|
Comparative Tracking Index (UL) {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
1.5
|
mm
|
UL 94
|
|
|
UL Recognized, 94-5VB Rating (3)
|
2.49
|
mm
|
UL 94
|
|
|
Source GMD, last updated:2011/09/19
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
75 - 80
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.04
|
%
|
|
Melt Temperature
|
230 - 275
|
°C
|
|
Nozzle Temperature
|
230 - 275
|
°C
|
|
Front - Zone 3 Temperature
|
225 - 275
|
°C
|
|
Middle - Zone 2 Temperature
|
215 - 260
|
°C
|
|
Rear - Zone 1 Temperature
|
210 - 255
|
°C
|
|
Mold Temperature
|
50 - 70
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
40 - 70
|
rpm
|
|
Shot to Cylinder Size
|
30 - 80
|
%
|
|
Vent Depth
|
0.038 - 0.076
|
mm
|