性能：通用级，Cycoloy PC/ABS，优秀的高耐热性，低温延性。
CYCOLOY? Resin C1200HF |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
PC+ABS, excellent flow/impact/high heat resistance. Low temperature ductility. For automotive, appliance and electrical components.
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
580
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
5
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
150
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 50 mm/min
|
23200
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
890
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
23900
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 50 mm/min
|
55
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
4.8
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
114
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
2360
|
MPa
|
ISO 527
|
|
|
Flexural Stress
|
86
|
MPa
|
ISO 178
|
|
|
Flexural Modulus
|
2250
|
MPa
|
ISO 178
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
59
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
49
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
553
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Total Energy, -30°C
|
553
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, notched, 23°C, 80*10*4mm, Cut
|
49
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched, -30°C, 80*10*4mm, Cut
|
34
|
kJ/m2
|
ISO 180/1A
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
129
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
112
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
7.2E-05
|
1/°C
|
ASTM E 831
|
|
|
Vicat Softening Temp, Rate B/50
|
130
|
°C
|
ISO 306
|
|
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
130
|
°C
|
ISO 75/Bf
|
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
110
|
°C
|
ISO 75/Af
|
|
|
Relative Temp Index, Elec
|
105
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
80
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
105
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.15
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/5.0 kgf
|
19
|
g/10 min
|
ASTM D 1238
|
|
|
Melt Volume Rate, MVR at 265°C/5.0 kg
|
24
|
cm3/10 min
|
ISO 1133
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Hot Wire Ignition {PLC)
|
3
|
PLC Code
|
UL 746A
|
|
|
High Ampere Arc Ign, surface {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
|
Comparative Tracking Index (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94HB Flame Class Rating (3)
|
1.19
|
mm
|
UL 94
|
|
|
Source GMD, last updated:2013/03/15
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
100 - 110
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
275 - 300
|
°C
|
|
Nozzle Temperature
|
275 - 300
|
°C
|
|
Front - Zone 3 Temperature
|
260 - 300
|
°C
|
|
Middle - Zone 2 Temperature
|
255 - 295
|
°C
|
|
Rear - Zone 1 Temperature
|
250 - 290
|
°C
|
|
Hopper Temperature
|
60 - 80
|
°C
|
|
Mold Temperature
|
60 - 90
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
40 - 70
|
rpm
|
|
Shot to Cylinder Size
|
30 - 80
|
%
|
|
Vent Depth
|
0.038 - 0.076
|
mm
|
898995850