性能：通用级，Cycoloy PC/ABS，高和延性在73 f和-20 f。
CYCOLOY? Resin C1110HF |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
High impact and ductility at 73F and -20F. For thin-wall applications.
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
600
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
5
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
75
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 50 mm/min
|
22400
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
880
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
24200
|
kgf/cm2
|
ASTM D 790
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
65
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
27
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Energy @ peak, 23°C
|
622
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Energy @ peak, -30
|
483
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Total Energy, 23°C
|
622
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Total Energy, -30°C
|
553
|
cm-kgf
|
ASTM D 3763
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
126
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
110
|
°C
|
ASTM D 648
|
|
|
CTE, -30°C to 30°C, flow
|
7.2E-05
|
1/°C
|
ASTM D 696
|
|
|
Relative Temp Index, Elec
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
60
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.14
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/3.8 kgf
|
12
|
g/10 min
|
ASTM D 1238
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Arc Resistance, Tungsten {PLC}
|
5
|
PLC Code
|
ASTM D 495
|
|
|
Hot Wire Ignition {PLC)
|
3
|
PLC Code
|
UL 746A
|
|
|
High Voltage Arc Track Rate {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
|
High Ampere Arc Ign, surface {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
|
Comparative Tracking Index (UL) {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94HB Flame Class Rating (3)
|
1.21
|
mm
|
UL 94
|
|
|
UV-light, water exposure/immersion
|
F2
|
-
|
UL 746C
|
|
|
Source GMD, last updated:2000/01/05
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
105 - 110
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.04
|
%
|
|
Melt Temperature
|
275 - 300
|
°C
|
|
Nozzle Temperature
|
275 - 300
|
°C
|
|
Front - Zone 3 Temperature
|
260 - 300
|
°C
|
|
Middle - Zone 2 Temperature
|
255 - 295
|
°C
|
|
Rear - Zone 1 Temperature
|
250 - 290
|
°C
|
|
Mold Temperature
|
60 - 90
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
40 - 70
|
rpm
|
|
Shot to Cylinder Size
|
30 - 80
|
%
|
|
Vent Depth
|
0.038 - 0.076
|
mm
|