性能：通用级，Cycoloy PC/ABS，高耐热性平衡，抗水解和热老化。
CYCOLOY? Resin XCY620S |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
PC+ ABS Automotive applications
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
870
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
23400
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 50 mm/min
|
54
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 50 mm/min
|
56
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
4.5
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
100
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
2200
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
82
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
2200
|
MPa
|
ISO 178
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Instrumented Impact Total Energy, 23°C
|
560
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Total Energy, -30°C
|
662
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, unnotched 80*10*3 +23°C
|
PASSES
|
kJ/m2
|
ISO 180/1U
|
|
|
Izod Impact, notched 80*10*4 +23°C
|
55
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*4 -30°C
|
40
|
kJ/m2
|
ISO 180/1A
|
|
|
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
60
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
|
45
|
kJ/m2
|
ISO 179/1eA
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
129
|
°C
|
ASTM D 1525
|
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
128
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
108
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
7.E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
7.E-05
|
1/°C
|
ASTM E 831
|
|
|
Ball Pressure Test, 75°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
|
Ball Pressure Test, approximate maximum
|
100
|
°C
|
IEC 60695-10-2
|
|
|
Vicat Softening Temp, Rate B/120
|
130
|
°C
|
ISO 306
|
|
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
126
|
°C
|
ISO 75/Bf
|
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
106
|
°C
|
ISO 75/Af
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.14
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Density
|
1.14
|
g/cm3
|
ISO 1183
|
|
|
Water Absorption, 23°C/24hrs
|
0.3
|
%
|
ISO 62-1
|
|
|
Water Absorption, (23°C/sat)
|
0.4
|
%
|
ISO 62
|
|
|
Moisture Absorption (23°C / 50% RH)
|
0.13
|
%
|
ISO 62
|
|
|
Melt Volume Rate, MVR at 260°C/5.0 kg
|
20
|
cm3/10 min
|
ISO 1133
|
|
|
Melt Volume Rate, MVR at 265°C/5.0 kg
|
25
|
cm3/10 min
|
ISO 1133
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Volume Resistivity
|
>1.E+16
|
Ohm-cm
|
IEC 60093
|
|
|
Surface Resistivity, ROA
|
>1.E+16
|
Ohm
|
IEC 60093
|
|
|
Dielectric Strength, in oil, 0.8 mm
|
39
|
kV/mm
|
IEC 60243-1
|
|
|
Dielectric Strength, in oil, 1.6 mm
|
25
|
kV/mm
|
IEC 60243-1
|
|
|
Dielectric Strength, in oil, 3.2 mm
|
17
|
kV/mm
|
IEC 60243-1
|
|
|
Source GMD, last updated:2013/03/26
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
95 - 105
|
°C
|
|
Drying Time
|
2 - 4
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
260 - 290
|
°C
|
|
Nozzle Temperature
|
240 - 280
|
°C
|
|
Front - Zone 3 Temperature
|
250 - 290
|
°C
|
|
Middle - Zone 2 Temperature
|
250 - 290
|
°C
|
|
Rear - Zone 1 Temperature
|
230 - 260
|
°C
|
|
Hopper Temperature
|
60 - 80
|
°C
|
|
Mold Temperature
|
60 - 90
|
°C
|
898995850