性能：通用级，Cycoloy PC/ABS，添加冲击改性剂，矿物增强，冲击改性，不透明。
CYCOLOY? Resin XCM851 |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
|
|
High heat PC/ABS blend offering high modulus / low CTE and good practical impact
|
|
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 5 mm/min
|
610
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
350
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
4
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
12
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
48400
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
1100
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
46300
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 5 mm/min
|
55
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 5 mm/min
|
45
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 5 mm/min
|
4
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 5 mm/min
|
10
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
4600
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
100
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
4400
|
MPa
|
ISO 178
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
10
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
8
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
611
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, unnotched 80*10*3 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
|
Izod Impact, notched 80*10*3 +23°C
|
12
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*3 -30°C
|
9
|
kJ/m2
|
ISO 180/1A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
|
15
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
|
|
|
|
|
|