CYCOLOY? Resin MC1300 |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
Cycoloy MC1300 resin is an injection moldable PC/ABS blend with excellent flow and impact performance. It is designed for plating applications mostly used in the automotive industry.
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
510
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
440
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
8.6
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
150
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 50 mm/min
|
21700
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
730
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
21000
|
kgf/cm2
|
ASTM D 790
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
54
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
43
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
414
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Total Energy, -30°C
|
345
|
cm-kgf
|
ASTM D 3763
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
111
|
°C
|
ASTM D 1525
|
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
115
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
98
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
7.2E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
9.E-05
|
1/°C
|
ASTM E 831
|
|
|
Thermal Conductivity
|
0.2
|
W/m-°C
|
ASTM C 177
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.1
|
-
|
ASTM D 792
|
|
|
Water Absorption, 24 hours
|
0.1
|
%
|
ASTM D 570
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.8
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/5.0 kgf
|
14
|
g/10 min
|
ASTM D 1238
|
|
|
Source GMD, last updated:1998/10/05
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
100 - 105
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.04
|
%
|
|
Melt Temperature
|
260 - 290
|
°C
|
|
Nozzle Temperature
|
260 - 290
|
°C
|
|
Front - Zone 3 Temperature
|
255 - 290
|
°C
|
|
Middle - Zone 2 Temperature
|
255 - 290
|
°C
|
|
Rear - Zone 1 Temperature
|
250 - 280
|
°C
|
|
Mold Temperature
|
75 - 100
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
40 - 70
|
rpm
|
|
Shot to Cylinder Size
|
30 - 80
|
%
|
|
Vent Depth
|
0.038 - 0.076
|
mm
|
|
Source GMD, last updated:1998/10/05
|