性能：通用级，Cycoloy PC/ABS，热稳定，冲击改性，稳定。
详细说明
CYCOLOY? Resin CY9640 |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
PC+ ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
560
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
530
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
4.7
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
115
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
23400
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
900
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
23400
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 50 mm/min
|
54
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 50 mm/min
|
51
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
4.5
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
115
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
2200
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
83
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
2200
|
MPa
|
ISO 178
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
65
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
48
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
571
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Total Energy, -30°C
|
713
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, notched 80*10*3 +23°C
|
70
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*3 -30°C
|
45
|
kJ/m2
|
ISO 180/1A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
|
70
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
|
45
|
kJ/m2
|
ISO 179/1eA
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
127
|
°C
|
ASTM D 1525
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
107
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
7.E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
7.E-05
|
1/°C
|
ASTM E 831
|
|
|
Thermal Conductivity
|
0.2
|
W/m-°C
|
ISO 8302
|
|
|
CTE, -40°C to 40°C, flow
|
8.E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, -40°C to 40°C, xflow
|
8.E-05
|
1/°C
|
ISO 11359-2
|
|
|
Ball Pressure Test, 75°C +/- 2°C
|
Pass
|
-
|
IEC 60695-10-2
|
|
|
Vicat Softening Temp, Rate B/50
|
127
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/120
|
129
|
°C
|
ISO 306
|
|
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
126
|
°C
|
ISO 75/Bf
|
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
105
|
°C
|
ISO 75/Af
|
|
|
Relative Temp Index, Elec
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
60
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.14
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/5.0 kgf
|
22
|
g/10 min
|
ASTM D 1238
|
|
|
Density
|
1.14
|
g/cm3
|
ISO 1183
|
|
|
Water Absorption, (23°C/sat)
|
0.4
|
%
|
ISO 62
|
|
|
Moisture Absorption (23°C / 50% RH)
|
0.15
|
%
|
ISO 62
|
|
|
Melt Volume Rate, MVR at 260°C/5.0 kg
|
21
|
cm3/10 min
|
ISO 1133
|
|
|
Melt Viscosity, 260°C, 1500 sec-1
|
195
|
Pa-s
|
ISO 11443
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Volume Resistivity
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
|
Surface Resistivity, ROA
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
|
Dielectric Strength, in oil, 0.8 mm
|
35
|
kV/mm
|
IEC 60243-1
|
|
|
Dielectric Strength, in oil, 1.6 mm
|
25
|
kV/mm
|
IEC 60243-1
|
|
|
Dielectric Strength, in oil, 3.2 mm
|
17
|
kV/mm
|
IEC 60243-1
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94HB Flame Class Rating (3)
|
1.5
|
mm
|
UL 94
|
|
|
UL Recognized, 94HB Flame Class Rating 2nd value (3)
|
3
|
mm
|
UL 94
|
|
|
Glow Wire Ignitability Temperature, 3.0 mm
|
750
|
°C
|
IEC 60695-2-13
|
|
|
Source GMD, last updated:2004/11/19
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
95 - 105
|
°C
|
|
Drying Time
|
2 - 4
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
260 - 290
|
°C
|
|
Nozzle Temperature
|
240 - 280
|
°C
|
|
Front - Zone 3 Temperature
|
250 - 290
|
°C
|
|
Middle - Zone 2 Temperature
|
250 - 290
|
°C
|
|
Rear - Zone 1 Temperature
|
230 - 260
|
°C
|
|
Hopper Temperature
|
60 - 80
|
°C
|
|
Mold Temperature
|
60 - 90
|
°C
|
898995850