性能：电镀级，可电镀Cycoloy PC/ABS。
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
530
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
470
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
4.2
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
110
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
24100
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
830
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
24100
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 50 mm/min
|
51
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 50 mm/min
|
47
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
4
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
100
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
2400
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
65
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
2200
|
MPa
|
ISO 178
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
57
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
38
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
560
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, notched 80*10*3 +23°C
|
50
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*3 -30°C
|
35
|
kJ/m2
|
ISO 180/1A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
|
50
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
|
35
|
kJ/m2
|
ISO 179/1eA
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
126
|
°C
|
ASTM D 1525
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
103
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
7.2E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
7.8E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, flow
|
7.2E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, -40°C to 40°C, xflow
|
7.8E-05
|
1/°C
|
ISO 11359-2
|
|
|
Ball Pressure Test, 75°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
|
Vicat Softening Temp, Rate B/50
|
126
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/120
|
129
|
°C
|
ISO 306
|
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
103
|
°C
|
ISO 75/Af
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.13
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.8
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/5.0 kgf
|
16
|
g/10 min
|
ASTM D 1238
|
|
|
Density
|
1.1
|
g/cm3
|
ISO 1183
|
|
|
Water Absorption, (23°C/sat)
|
0.4
|
%
|
ISO 62
|
|
|
Moisture Absorption (23°C / 50% RH)
|
0.2
|
%
|
ISO 62
|
|
|
Melt Volume Rate, MVR at 265°C/5.0 kg
|
20
|
cm3/10 min
|
ISO 1133
|
|
|
Source GMD, last updated:2004/12/21
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
100 - 105
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.04
|
%
|
|
Melt Temperature
|
260 - 290
|
°C
|
|
Nozzle Temperature
|
260 - 290
|
°C
|
|
Front - Zone 3 Temperature
|
255 - 290
|
°C
|
|
Middle - Zone 2 Temperature
|
255 - 290
|
°C
|
|
Rear - Zone 1 Temperature
|
250 - 280
|
°C
|
|
Mold Temperature
|
75 - 100
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
40 - 70
|
rpm
|
|
Shot to Cylinder Size
|
30 - 80
|
%
|
|
Vent Depth
|
0.038 - 0.076
|
mm
|