性能：通用级，PC/ABS，高模量。
CYCOLOY? Resin CM6210 |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection molding applications where higher stiffness is needed.
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 5 mm/min
|
650
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
500
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
4.9
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
80
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
36400
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
1120
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
35600
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 5 mm/min
|
59
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 5 mm/min
|
65
|
MPa
|
ISO 527
|
|
|
Tensile Stress, yield, 50 mm/min
|
63
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 50 mm/min
|
50
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 5 mm/min
|
3.6
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 5 mm/min
|
101
|
%
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
3.5
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
97
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
3660
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
106
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
3560
|
MPa
|
ISO 178
|
|
|
Hardness, Rockwell R
|
98
|
-
|
ISO 2039-2
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
50
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
9
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
458
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, notched 80*10*3 +23°C
|
45
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*3 -30°C
|
10
|
kJ/m2
|
ISO 180/1A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
|
45
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
|
10
|
kJ/m2
|
ISO 179/1eA
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
106
|
°C
|
ASTM D 1525
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
90
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
5.7E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
7.E-05
|
1/°C
|
ASTM E 831
|
|
|
Thermal Conductivity
|
0.3
|
W/m-°C
|
ISO 8302
|
|
|
CTE, -40°C to 40°C, flow
|
5.2E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, -40°C to 40°C, xflow
|
6.E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, 23°C to 60°C, flow
|
5.2E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, 23°C to 60°C, xflow
|
6.E-05
|
1/°C
|
ISO 11359-2
|
|
|
Ball Pressure Test, 75°C +/- 2°C
|
pass
|
-
|
IEC 60695-10-2
|
|
|
Ball Pressure Test, approximate maximum
|
95
|
°C
|
IEC 60695-10-2
|
|
|
Vicat Softening Temp, Rate B/50
|
112
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/120
|
114
|
°C
|
ISO 306
|
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
99
|
°C
|
ISO 75/Be
|
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
89
|
°C
|
ISO 75/Ae
|
|
|
Relative Temp Index, Elec
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
60
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.28
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.4 - 0.6
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/5.0 kgf
|
11.5
|
g/10 min
|
ASTM D 1238
|
|
|
Density
|
1.27
|
g/cm3
|
ISO 1183
|
|
|
Water Absorption, (23°C/sat)
|
0.3
|
%
|
ISO 62
|
|
|
Moisture Absorption (23°C / 50% RH)
|
0.1
|
%
|
ISO 62
|
|
|
Melt Volume Rate, MVR at 260°C/5.0 kg
|
9
|
cm3/10 min
|
ISO 1133
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Dielectric Strength, in oil, 0.8 mm
|
38
|
kV/mm
|
IEC 60243-1
|
|
|
Dielectric Strength, in oil, 1.6 mm
|
26
|
kV/mm
|
IEC 60243-1
|
|
|
Dielectric Strength, in oil, 3.2 mm
|
17
|
kV/mm
|
IEC 60243-1
|
|
|
Relative Permittivity, 1 MHz
|
2.8
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 50/60 Hz
|
0.003
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 1 MHz
|
0.004
|
-
|
IEC 60250
|
|
|
Comparative Tracking Index
|
250
|
V
|
IEC 60112
|
|
|
Relative Permittivity, 50/60 Hz
|
2.9
|
-
|
IEC 60250
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
1.5
|
mm
|
UL 94
|
|
|
Source GMD, last updated:2005/02/08
|
|
Processing
|
|
? Barrel temperatures should be banked TO 150°C (300°F)
|
| Parameter | ||
|
Sheet Extrusion
|
Value | Unit |
|
Drying Temperature
|
80 - 90
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
12
|
hrs
|
|
Minimum Moisture Content
|
0.04
|
%
|
|
Melt Temperature
|
220 - 245
|
°C
|
|
Barrel - Zone 1 Temperature
|
180 - 225
|
°C
|
|
Barrel - Zone 2 Temperature
|
190 - 230
|
°C
|
|
Barrel - Zone 3 Temperature
|
205 - 240
|
°C
|
|
Barrel - Zone 4 Temperature
|
210 - 245
|
°C
|
|
Adapter Temperature
|
210 - 245
|
°C
|
|
Die Temperature
|
210 - 245
|
°C
|
|
Roll Stack Temp - Top
|
70 - 100
|
°C
|
|
Roll Stack Temp - Middle
|
70 - 95
|
°C
|
|
Roll Stack Temp - Bottom
|
65 - 90
|
°C
|
898995850