性能：通用级，阻燃剂填充PC/ABS。
CYCOLOY? Resin CM6140 |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
Cycoloy resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffness, balanced properties in flow, impact and heat designed for various thin wall applications.
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
660
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, yld, Type I, 5 mm/min
|
660
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
500
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
4
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
100
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
35600
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
1010
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
33600
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, break, 5 mm/min
|
50
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 5 mm/min
|
3.5
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
15
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
3200
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
97
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
3450
|
MPa
|
ISO 178
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
20
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
8
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
509
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, notched 80*10*3 +23°C
|
10
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*3 -30°C
|
5
|
kJ/m2
|
ISO 180/1A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
|
10
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
|
5
|
kJ/m2
|
ISO 179/1eA
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
91
|
°C
|
ASTM D 1525
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
83
|
°C
|
ASTM D 648
|
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
97
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
89
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
5.5E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
6.E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, flow
|
5.5E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, -40°C to 40°C, xflow
|
6.E-05
|
1/°C
|
ISO 11359-2
|
|
|
Ball Pressure Test, 75°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
|
Vicat Softening Temp, Rate B/50
|
98
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/120
|
102
|
°C
|
ISO 306
|
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
80
|
°C
|
ISO 75/Af
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.26
|
-
|
ASTM D 792
|
|
|
Water Absorption, 24 hours
|
0.1
|
%
|
ASTM D 570
|
|
|
Moisture Absorption, 50% RH, 24 hrs
|
0.01
|
%
|
ASTM D 570
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.3 - 0.5
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.4 - 0.6
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/2.16 kgf
|
17.5
|
g/10 min
|
ASTM D 1238
|
|
|
Density
|
1.25
|
g/cm3
|
ISO 1183
|
|
|
Water Absorption, (23°C/sat)
|
0.09
|
%
|
ISO 62
|
|
|
Moisture Absorption (23°C / 50% RH)
|
0.01
|
%
|
ISO 62
|
|
|
Melt Volume Rate, MVR at 220°C/5.0 kg
|
14
|
cm3/10 min
|
ISO 1133
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Volume Resistivity
|
2.68E+16
|
Ohm-cm
|
ASTM D 257
|
|
|
Surface Resistivity
|
3.54E+15
|
Ohm
|
ASTM D 257
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94V-1 Flame Class Rating (3)
|
0.6
|
mm
|
UL 94
|
|
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
0.8
|
mm
|
UL 94
|
|
|
UL Recognized, 94-5VB Rating (3)
|
1.5
|
mm
|
UL 94
|
|
|
Glow Wire Flammability Index 960°C, passes at
|
0.8
|
mm
|
IEC 60695-2-12
|
|
|
Glow Wire Ignitability Temperature, 1.0 mm
|
850
|
°C
|
IEC 60695-2-13
|
|
|
Glow Wire Ignitability Temperature, 3.0 mm
|
800
|
°C
|
IEC 60695-2-13
|
|
|
Source GMD, last updated:2004/12/02
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
90
|
°C
|
|
Drying Time
|
>4
|
hrs
|
|
Maximum Moisture Content
|
0.04
|
%
|
|
Melt Temperature
|
275 - 300
|
°C
|
|
Nozzle Temperature
|
280 - 300
|
°C
|
|
Front - Zone 3 Temperature
|
280 - 300
|
°C
|
|
Middle - Zone 2 Temperature
|
275 - 300
|
°C
|
|
Rear - Zone 1 Temperature
|
275 - 300
|
°C
|
|
Mold Temperature
|
60 - 80
|
°C
|