性能：通用级，耐高温，冲击改性树脂，阻燃。
CYCOLOY? Resin CH6410 |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
CH6410 is a high heat, impact modified PC resin, with nonbrominated, nonchlorinated flame retardant system. Limited colors only.
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
640
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
550
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
5.5
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
88
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 50 mm/min
|
25900
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
970
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
26500
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 50 mm/min
|
63
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 50 mm/min
|
55
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
5
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
95
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
2300
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
90
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
2400
|
MPa
|
ISO 178
|
|
|
Hardness, H358/30
|
100
|
MPa
|
ISO 2039-1
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
92
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
740
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, notched 80*10*4 +23°C
|
50
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*4 0°C
|
19
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*4 -30°C
|
15
|
kJ/m2
|
ISO 180/1A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
55
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
|
15
|
kJ/m2
|
ISO 179/1eA
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
127
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
118
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
7.74E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
5.94E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, 23°C to 60°C, flow
|
7.E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, 23°C to 60°C, xflow
|
7.E-05
|
1/°C
|
ISO 11359-2
|
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
|
Vicat Softening Temp, Rate B/50
|
134
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/120
|
135
|
°C
|
ISO 306
|
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
126
|
°C
|
ISO 75/Be
|
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
113
|
°C
|
ISO 75/Ae
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.19
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage on Tensile Bar, flow (2) (5)
|
0.05 - 0.07
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.4 - 0.5
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/2.16 kgf
|
6.3
|
g/10 min
|
ASTM D 1238
|
|
|
Density
|
1.2
|
g/cm3
|
ISO 1183
|
|
|
Melt Volume Rate, MVR at 260°C/5.0 kg
|
16
|
cm3/10 min
|
ISO 1133
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Volume Resistivity
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
|
Surface Resistivity, ROA
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
|
Dielectric Strength, in oil, 3.2 mm
|
18
|
kV/mm
|
IEC 60243-1
|
|
|
Relative Permittivity, 1 MHz
|
2.7
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 50/60 Hz
|
0.001
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 1 MHz
|
0.01
|
-
|
IEC 60250
|
|
|
Comparative Tracking Index
|
225
|
V
|
IEC 60112
|
|
|
Relative Permittivity, 50/60 Hz
|
2.7
|
-
|
IEC 60250
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94V-1 Flame Class Rating (3)
|
0.99
|
mm
|
UL 94
|
|
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
1.49
|
mm
|
UL 94
|
|
|
Source GMD, last updated:2002/10/29
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
90 - 100
|
°C
|
|
Drying Time
|
2 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.04
|
%
|
|
Melt Temperature
|
270 - 300
|
°C
|
|
Nozzle Temperature
|
265 - 300
|
°C
|
|
Front - Zone 3 Temperature
|
265 - 300
|
°C
|
|
Middle - Zone 2 Temperature
|
260 - 300
|
°C
|
|
Rear - Zone 1 Temperature
|
260 - 300
|
°C
|
|
Mold Temperature
|
60 - 90
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
40 - 70
|
rpm
|
|
Shot to Cylinder Size
|
40 - 80
|
%
|
|
Vent Depth
|
0.038 - 0.076
|
mm
|