性能：通用级，Cycoloy PC/ABS，冲击改性。
CYCOLOY? Resin C8080REC |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
PC+ABS Recycle Resin with good flow, good temperature resistance and moderate impact
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
570
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
560
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
4.6
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
110
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 50 mm/min
|
26000
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
940
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
25400
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 50 mm/min
|
56
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 50 mm/min
|
47
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
5
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
85
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
2380
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
92
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
2480
|
MPa
|
ISO 178
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
70
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
20
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
576
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Total Energy, -30°C
|
518
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Total Energy, -40°C
|
541
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, notched 80*10*4 +23°C
|
51
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*4 -30°C
|
17
|
kJ/m2
|
ISO 180/1A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
54
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
|
19
|
kJ/m2
|
ISO 179/1eA
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
127
|
°C
|
ASTM D 1525
|
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
126
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
107
|
°C
|
ASTM D 648
|
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
129
|
°C
|
ISO 75/Be
|
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
113
|
°C
|
ISO 75/Ae
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.17
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.6 - 0.9
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.6 - 0.9
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 300°C/1.2 kgf
|
13
|
g/10 min
|
ASTM D 1238
|
|
|
Density
|
1.17
|
g/cm3
|
ISO 1183
|
|
|
Source GMD, last updated:2013/01/30
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
105 - 110
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.04
|
%
|
|
Melt Temperature
|
275 - 300
|
°C
|
|
Nozzle Temperature
|
275 - 300
|
°C
|
|
Front - Zone 3 Temperature
|
260 - 300
|
°C
|
|
Middle - Zone 2 Temperature
|
255 - 295
|
°C
|
|
Rear - Zone 1 Temperature
|
250 - 290
|
°C
|
|
Mold Temperature
|
60 - 90
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
40 - 70
|
rpm
|
|
Shot to Cylinder Size
|
30 - 80
|
%
|
|
Vent Depth
|
0.038 - 0.076
|
mm
|