性能：通用级，Cycoloy PC/ABS。
CYCOLOY? Resin C6600 |
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
Nonbrominated, nonchlorinated FR PC+ABS with balanced flow, impact and hydrolytic stability for a wide variety of applications including business equipment, monitors, enclosures, among others.
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
640
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
490
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
4
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
80
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 50 mm/min
|
30500
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
950
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
26700
|
kgf/cm2
|
ASTM D 790
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
56
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
520
|
cm-kgf
|
ASTM D 3763
|
|
|
Instrumented Impact Total Energy, -30°C
|
520
|
cm-kgf
|
ASTM D 3763
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
99
|
°C
|
ASTM D 1525
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
83
|
°C
|
ASTM D 648
|
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
98
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
90
|
°C
|
ASTM D 648
|
|
|
Relative Temp Index, Elec
|
80
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
70
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
80
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.19
|
-
|
ASTM D 792
|
|
|
Water Absorption, 24 hours
|
0.11
|
%
|
ASTM D 570
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.4 - 0.6
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 260°C/2.16 kgf
|
21.5
|
g/10 min
|
ASTM D 1238
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Volume Resistivity
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
|
Surface Resistivity, ROA
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
|
Dielectric Strength, in oil, 3.2 mm
|
17
|
kV/mm
|
IEC 60243-1
|
|
|
Relative Permittivity, 1 MHz
|
2.7
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 50/60 Hz
|
0.004
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 1 MHz
|
0.006
|
-
|
IEC 60250
|
|
|
Relative Permittivity, 50/60 Hz
|
2.7
|
-
|
IEC 60250
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94V-2 Flame Class Rating (3)
|
0.75
|
mm
|
UL 94
|
|
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
1.5
|
mm
|
UL 94
|
|
|
UL Recognized, 94-5VB Rating (3)
|
2
|
mm
|
UL 94
|
|
|
Source GMD, last updated:2005/07/25
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
80 - 90
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.04
|
%
|
|
Melt Temperature
|
245 - 275
|
°C
|
|
Nozzle Temperature
|
245 - 275
|
°C
|
|
Front - Zone 3 Temperature
|
245 - 275
|
°C
|
|
Middle - Zone 2 Temperature
|
220 - 275
|
°C
|
|
Rear - Zone 1 Temperature
|
220 - 255
|
°C
|
|
Mold Temperature
|
60 - 80
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
40 - 70
|
rpm
|
|
Shot to Cylinder Size
|
30 - 80
|
%
|
|
Vent Depth
|
0.038 - 0.076
|
mm
|