奥地利伯乐FOX CEL 75G E7010-G焊条原High cellulose type medicine kawadate down electrode. Arc blow force, side welding molding, less slag, easy cleaning, welding, forming beautiful wave, welding speed, weld metal has good mechanical properties, and has excellent anti air and anti cracking performance, is the joint vertical down welding electrode for all POSTTTION loop pipeline site, using dcrp. Use: for the butt welding of the carbon steel pipe, is also suitable for vertical down welding general carbon steel structure. Chemical comPOSTTTION of deposited metal (%) C Mn Si S chemical comPOSTTTION P Mo to ensure that the value of less than 0.20 0.4~0.6 is less than or equal to 0.2 than 0.035 than 0.040 ~0.40 test on mechanical properties of deposited metal project Rm (MPa) ReL or Rp0.2 (Mpa) A (%) KV2 (J) = 490 = 400 = guarantee value 20 = 27 (-30 C) 500~620 410~480 20~26 50~100 general results of X - ray detection: II reference current (DC+) electrode diameter (mm) Phi 3.2 Phi 4 welding current (A) 80~100 110~130奥地利伯乐BOHLER焊接材料 品名 AWS型号 熔敷金属化学成份（%） 熔敷金属力学性能 特性与用途 C Mn Si Cr Ni 其它 σ 0.2 (Mpa)　　 δ b (Mpa) δ(%) IV(J) FOX CEL E6010 0.12 0.5 0.14 - - 450 550 26 -20℃/95 纤维素钠型立向下管道（APIX42-X56）焊接用焊条 FOX CEL75 E7010-P1 0.14 1.0 0.14 - - 490 560 23 -20℃/85 纤维素钠型立向下管道（APIX56-X60）焊接用焊条 FOX CEL85 E8010-P1 0.14 0.7 0.10 - 0.6 550 600 24 -20℃/80 纤维素钠型立向下管道（APIX60-X70）焊接用焊条 FOX CEL90 E9010-G 0.14 0.8 0.14 - 0.6 Mo:0.9 610 650 21 -20℃/75 纤维素钠型立向下管道（APIX70-X80）焊接用焊条 FOX BVD85 E8018-G 0.04 0.9 0.40 - 0.6 510 560 27 -20℃/120 -40℃/70 碱性立向下管道（APIX65）焊接用焊条 FOX BVD90 E9018-G 0.04 1.2 0.40 - 2.2 600 650 27 -20℃/115 -40℃/80 碱性立向下管道（APIX70-X80）焊接用焊条品名 AWS型号 熔敷金属化学成份（%） 熔敷金属力学性能 特性与用途 C Mn Si Cr Ni 其它 σ0.2(Mpa)　　 δb(Mpa) δ(%) IV(J) FOX CEL E6010 0.12 0.5 0.14 - - 450 550 26 -20℃/95 纤维素钠型立向下管道（APIX42-X56）焊接用焊条 FOX CEL75 E7010-P1 0.14 1.0 0.14 - - 490 560 23 -20℃/85 纤维素钠型立向下管道（APIX56-X60）焊接用焊条 FOX CEL85 E8010-P1 0.14 0.7 0.10 - 0.6 550 600 24 -20℃/80 纤维素钠型立向下管道（APIX60-X70）焊接用焊条 FOX CEL90 E9010-G 0.14 0.8 0.14 - 0.6 Mo:0.9 610 650 21 -20℃/75 纤维素钠型立向下管道（APIX70-X80）焊接用焊条 FOX BVD85 E8018-G 0.04 0.9 0.40 - 0.6 510 560 27 -20℃/120 -40℃/70 碱性立向下管道（APIX65）焊接用焊条 FOX BVD90 E9018-G 0.04 1.2 0.40 - 2.2 600 650 27 -20℃/115 -40℃/80 碱性立向下管道（APIX70-X80）焊接用焊条 FOX 20MVW - 0.17 0.8 0.40 11.0 0.5 Mo:0.9 V:0.3 W:0.5 600 800 18 45 用于水轮机及锅炉中抗蠕变的热处理12%Cr钢的焊条 20MVW-IG - 0.21 0.6 0.40 11.3 - Mo:1.0 V:0.3 W:0.45 570 780 18 60 TIG焊丝，用途同FOX 20MVW FOX 13/4-25 E410NiMo 0.04 0.5 0.30 12.2 4.5 Mo:0.5 680 910 17 66 焊耐蒸汽、海水腐蚀的Cr13-Ni4钢，如水轮机，压缩机，蒸汽动力设备 FOX CN 22/9 E2209-17 0.03 0.8 0.90 22.5 9.0 Mo:3.2 N:0.15 640 800 24 56 双相不锈钢焊条，用于近海技术及化学工业，抗应力腐蚀好 CN 22/9-IG ER2209 0.02 1.7 0.60 22.5 9.2 Mo:3.2 N:0.13 600 800 33 150 TIG/MIG焊丝，用途同FOX CN 22/9 WIRE CN 22/9N-UP FLUX BB202 ER2209~SB20.9.3 0.02 1.6 0.4 22.0 8.4 Mo:2.7 N:0.13 610 780 28 60 埋弧焊用焊丝-焊剂组合，用途同FOX CN 22/9 FOX NIBAS 70/20 ENiCrFe-3 0.04 5.0 0.4 19.0 >67 Mo:4.5 Nb:2.0 420 680 40 -196℃/80 镍基合金焊条，适于-196℃- +550℃压力容器的制造，耐1200℃高温 NIBAS 70/20-IG ERNiCr-3 0.03 3.0 0.30 20.0 余 Nb:2.5 440 680 42 -196℃/100 TIG/MIG焊丝，用途同FOX NIBAS 70/20 FOX NIBAS 625 ENiCrMo-3 0.03 0.2 0.40 21.0 62.0 Mo:9.0 Nb:3.4 530 800 40 -196℃/45 钼镍基合金焊条，焊接高温，耐塑性变形及低温材料 NIBAS 625-IG ERNiCrMo-3 0.02 0.3 0.20 21.5 >60 Mo:9.0 Nb:3.6 540 800 38 -196℃/130 TIG/MIG焊丝，用途同FOX NIBAS 625 FOX NUT - 开槽割条，可在铸铁，合金堆焊层上开槽，切割 　 伯乐焊材牌号与对应标准品名 牌号 型号（AWS） 电焊条 FOX CEL E6010 电焊条 FOX CEL75 E7010 -P1 电焊条 FOX CEL85 E8010 -P1 电焊条 FOX CEL90 E9010-G 电焊条 FOX BVD85 E8018-G 电焊条 FOX BVD90 E9018-G 电焊条 FOX CEL 75G E7010-G 电焊条 FOX CEL 85G E8010-G 电焊条 FOX CN 22/9 N E2209-17电焊条 FOX CN 22/9 N-B E2209-15

品名 类别 AWS型号 元素化学成份百分比 C Si Mn Cr Ni Mo 不锈钢 焊条 308L/MVR E308L-17 0.02 0.8 1.0 20.0 10.5 308L/MVR E308L-15 0.03 0.2 1.7 20.0 10.0 308L/MVR E308L-16 0.03 0.3 1.5 20.0 10.0 308/308H E308H-17 0.06 0.7 1.1 20.0 10.0 347/MVNb E347-17 0.02 0.8 0.8 19.5 10.0 347/MVNb E347-15 0.06 0.2 1.7 19.5 10.0 316L/SKR E316L-17 0.02 0.8 1.1 18.5 12.0 2.8 316L/SKR E316L-15 0.03 0.2 1.7 18.5 12.0 2.8 316L/SKR E316L-16 0.02 0.3 1.4 19.0 12.0 2.8 316/316H E316H-17 0.06 0.8 1.0 19.0 12.0 2.8 318/SKNb E318-17 0.02 0.8 0.8 18.5 12.0 2.8 318/SKNb E318-15 0.04 0.2 2.1 18.5 12.5 2.7 317L/SNR E317L-17 0.02 0.7 0.9 19.0 13.0 3.7 2205 E2209-17 0.02 0.8 0.7 23.0 9.5 3.0 2205 E2209-15 0.02 0.5 0.8 23.0 9.5 3.0 904L E385-17 0.02 0.8 1.2 20.5 25.0 4.5 383 E383-17 0.02 0.9 0.9 27.0 32.0 3.7 P12-R EniCrMo-12 0.02 0.4 0.4 21.5 9.5 P625 EniCrMo-3 0.02 0.5 0.2 21.5 9.5 307 E307-17 0.07 0.8 4.0 20.0 10.5 0.8 309L E309L-15 0.03 0.2 1.9 24.0 13.0 P5 E309MoL-17 0.02 0.8 1.1 22.5 13.5 2.7 P5 E309MoL-15 0.03 0.2 2.0 22.5 13.0 2.7 P5 E309MoL-16 0.03 0.3 1.4 22.5 13.5 2.7 P7 E312-17 0.09 0.8 0.8 29.0 9.5 P10 ENiCrFe-3 0.02 0.4 6.5 16.0 309 E309-17 0.05 0.8 1.0 24.0 13.5 310 E310-17 0.10 0.5 2.1 26.0 21.0 310 E310-15 0.12 0.3 2.4 25.5 21.0品名 AWS型号 特 性 与 用 途 PIPEMASTER PRO60 E6010 纤维素焊条，可用于X42到X65大直径管线焊接，也可用于X52-X70钢管的根焊。 PIPEMASTER 70 E7010-P1 纤维素焊条，可用于X52到X65钢大直径管线焊接。 PIPEMASTER 80 E8010-P1 纤维素焊条，可用于X56到X70钢大直径管线焊接。 PIPEMASTER 90 E9010-G 纤维素焊条，可用于X65到X80钢大直径管线焊接。 低合金钢焊条 品名 AWS型号 特 性 与 用 途 HOBART 7018XLM E7018-1 H4R 难吸潮超低氢焊条，低温韧性好，可用于锅炉、压力容器等焊接。 HOBART 7016 E7016 H4 低氢型焊条全位置焊接性能好，用于X80钢管的根焊（上坡焊）。 HOBART 718XC E7018-1 H4R 难吸潮超低氢焊条，低温韧性好，焊接重要结构。 HOBART 7018A1 E7018A1 H4R 用于焊接0.5% Mo钢,也可用于管线焊接。 HOBART 8018B2 E8018-B2 H4R 低氢耐热钢焊条，焊接1.25Cr-0.5Mo钢。 HOBART 8018B2L E8018-B2LH4R 焊碳比8018B2低,韧性好，焊接1.25Cr-0.5Mo钢,可降低预热温度。 HOBART 8018C1 E8018-C1 H4R 用于焊接低温工作的储气罐等。 HOBART 8018C2 E8018-C2 H4R 用于焊接低温工作的3.5Ni钢制储气罐。 HOBART 8018C3 E8018-C3 H4R 用于焊接60公斤级高强钢及1%Ni钢。 HOBART 9018B3 E9018-B3 H4R 低氢耐热钢焊条，焊接2.25Cr-1Mo钢。 HOBART 9018B3L E9018-B3LH4R 焊碳比9018B3低,抗裂性好。 HOBART 9018M E9018-M H4R 焊接HY80、HY90、T-1等高强钢。 HOBART 10018D2 E10018-D2 H4R 焊接Mn-Mo型钢，压力容器部件或铸钢件。 HOBART 11018M E11018-M H4R 焊接HY80、HY90、HY100及低合金高强钢。 HOBART 12018M E12018-M H4R 焊接相应强度的低合金钢结构Baso® 48 SP  E7018-1 H8用于低温钢结构的对接焊及角焊，该焊条符合AWS A5.1E7018-1

Baso® 49    E7018 H4难吸潮超低氢焊条，低温韧性好，可用于锅炉、压力容器等焊接
Baso® 51P   E7018-1用于低温钢结构的对接焊及角焊，该焊条符合AWS A5.1E7018-1
Baso® 100   E7016 H4R低氢型焊条全位置焊接性能好，用于X80钢管的根焊（上坡焊）。
 Baso® 120   E7018 H4R难吸潮超低氢焊条，低温韧性好，可用于锅炉、压力容器等焊接
Baso® G     E7018-1 H4R难吸潮超低氢焊条，低温韧性好，可用于锅炉、压力容器等焊接
Baso® 26V   E 7048 H8用于管道的对接焊.向下立焊时焊接工艺性能优良，焊缝金属具有良好的力学性能
Conarc® 48   E7018-1 H4R难吸潮超低氢焊条，低温韧性好，可用于锅炉、压力容器等焊接
Conarc® 49   E7018 H4R难吸潮超低氢焊条，低温韧性好，焊接重要结构
Conarc® 49C  E7018-1 H4R难吸潮超低氢焊条，低温韧性好，可用于锅炉、压力容器等焊接
Conarc® 51   E7016-1 H4R低氢型焊条全位置焊接性能好，用于X80钢管的根焊（上坡焊）
LINCOLN® 7018-1  E7018-1用于低温钢结构的对接焊及角焊
Conarc® L150   E7028 H4R用于横角焊,烘干:70～100℃×0.5～1h
Conarc® V180   E7028 H4R用于横角焊,烘干:70～100℃×0.5～1h
Kardo®     E6018该焊条是典型的钛钙型焊条
Shield Arc® HYP+  E 7010-P1尤其适用于钢种为X56和X60或L385M/L415MB的管材
Shield Arc® 70+    E8010-G纤维素焊条，可用于X56到X70钢大直径管线焊接
Shield Arc® 90    E 9010-G保证焊缝熔敷金属的优良机械性能、最高金相质量和可靠性
Shield Arc® 6P+   E6010用于垂直下向焊接直流负极的根焊再接直流正极的热焊、填充、盖面焊
Shield Arc® 7P+    E7010-P1/E7010-G尤其适用于钢种为X56和X60或L385M/L415MB的管材
Shield Arc® 8P+    E8010-P1是最常用且适应性强纤维素焊条，它能极其充分地满足横贯国家的管道实地焊接的各种严格的要求
Conarc® 55CT    E8018-W2-H4R焊接HY80、HY90、T-1等高强钢
Conarc® 60G     E9018M-H4焊接HY80、HY90、T-1等高强钢
Conarc® 70G   E9018-G-H4焊接HY80、HY90、T-1等高强钢
Conarc® 80   E11018M-H4焊接Mn-Mo型钢，压力容器部件或铸钢件
Conarc® 85   E12018-G-H4R焊接相应强度的低合金钢结构
Kryo® 1     E7018-G-H4R耐大气腐蚀性能优良，用于桥梁，铁路，港口机械等钢结构的焊接
Kryo® 1N    E8016-G-H4R耐吸潮超低氢焊条，焊接低温钢，力学性能优良，适合厚板重要结构
Kryo® 1P    E8018-G-H4R耐吸潮超低氢焊条，焊接低温钢，力学性能优良，适合厚板重要结构
Kryo® 1-180   E8018-G-H4R耐吸潮超低氢焊条，焊接低温钢，力学性能优良，适合厚板重要结构
Kryo® 2    E9018-G-H4R超低氢焊条，抗裂性能优良，用于焊接屈服强度610Mpa的高强钢
Kryo® 3    E8018-C1-H4低温钢焊条，焊接3.5Ni钢，焊态和热处理后力学性能优良
Kryo® 4    E7016-C2L-H4R用于焊接0.5%Mo钢，也可用于管线焊接
SL®12G    E7018-A1-H4R用于焊接0.5%Mo钢，也可用于管线焊接
SL®19G    E8018-B2-H4焊接和堆焊Cr:1.25,Mo:0.5铬钼钢，适合STC（步冷热处理）焊接
SL®19G(STC)   E8018-B2-H4焊接和堆焊Cr:1.25,Mo:0.5铬钼钢，适合STC（步冷热处理）焊接
SL®20G        E9018-B3-H4焊接和堆焊Cr:2.25-Mo铬钼钢，适合STC（步冷热处理）焊接
SL®20G(STC)    E9018-B3-H4焊接和堆焊Cr:2.25-Mo铬钼钢，适合STC（步冷热处理）焊接
SL®22G      E8018-B1-H4焊接和堆焊Cr:1.25,Mo:0.5铬钼钢
SL®502      E8018-B6-H4R焊接和堆焊Cr:4-6%,Mo:0.5铬钼钢
SL®9Cr(P91)  E9016-B9-H4焊接和堆焊Cr:8-11%,Mo:2铬钼钢，焊接P91.T91钢