原料技术数据
|
性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
|
|
基本性能 |
熔体流动速率 |
200℃/5kg |
ASTM D-1238 |
3.0 |
g/10min |
|
物理性能 |
比重 |
|
ASTM D-792 |
1.04 |
g/cm3 |
|
模具收缩率 |
|
ASTM D-955 |
0.40-0.70 |
% |
|
|
机械性能 |
拉伸强度 |
|
ASTM D-638 |
33.8 |
MPa |
|
断裂伸长率 |
|
ASTM D-638 |
55 |
% |
|
|
弯曲模量 |
|
ASTM D-790 |
2070 |
MPa |
|
|
弯曲强度 |
|
ASTM D-790 |
60.0 |
MPa |
|
|
IZOD缺口冲击强度 |
23℃ |
ASTM D-256 |
107 |
J/m |
|
|
热性能 |
热变形温度 |
1.80MPa，未退火 |
ASTM D-648 |
75.0 |
℃ |
|
热变形温度 |
1.80MPa，退火 |
ASTM D-648 |
98.9 |
℃ |
|
|
维卡软化温度 |
|
ASTM D-1525 |
106 |
℃ |
|
|
CLTE |
Flow |
ASTM D-696 |
0.000076 |
cm/cm/℃ |
|
|
阻燃性 |
1.50mm |
UL 94 |
HB |
|
|
|
光学性能 |
光泽度 |
60℃ |
ASTM D-523 |
92 |
|