10％玻璃纤维填充注塑级优化的热老化和紫外线稳定性，非常良好的流动性;拉伸模量= 4800兆帕;耐热性高;维卡/ B 120 = 134°C 。
[Datasheet Bayblend T88 GF-10]
| Property | Test Condition | Unit | Standard | typical Value | |
|---|---|---|---|---|---|
| Rheological properties | |||||
| Molding shrinkage, parallel | 150x105x3 mm; 260 °C / MT 80 °C | % | b.o. ISO 2577 | 0.25 - 0.45 | |
| Molding shrinkage, normal | 150x105x3 mm; 260 °C / MT 80 °C | % | b.o. ISO 2577 | 0.35 - 0.55 | |
| Melt viscosity | 1000 s-1; 260 °C | Pa·s | b.o. ISO 11443-A | 205 | |
| Mechanical properties (23 °C/50 % r. h.) | |||||
|
Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 4800 |
| Yield stress | 5 mm/min | MPa | ISO 527-1,-2 | 100 | |
| Yield strain | 5 mm/min | % | ISO 527-1,-2 | 3.2 | |
|
|
Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 95 |
|
|
Strain at break | 5 mm/min | % | ISO 527-1,-2 | 3.7 |
| Izod impact strength | 23 °C | kJ/m2 | ISO 180-U | 35 | |
| Izod impact strength | -30 °C | kJ/m2 | ISO 180-U | 35 | |
| Izod notched impact strength | 23 °C | kJ/m2 | ISO 180-A | 8.0 | |
| Izod notched impact strength | -30 °C | kJ/m2 | ISO 180-A | 6.0 | |
| Thermal properties | |||||
|
|
Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 121 |
|
|
Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 133 |
|
|
Vicat softening temperature | 50 N; 50 °C/h | °C | ISO 306 | 132 |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 134 | |
|
|
Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.4 |
|
|
Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.67 |
|
|
Burning behavior UL 94 [UL recognition] | 0.85 mm | Class | UL 94 | HB |
| Electrical properties (23 °C/50 % r. h.) | |||||
|
|
Relative permittivity | 100 Hz | - | IEC 60250 | 3.2 |
|
|
Relative permittivity | 1 MHz | - | IEC 60250 | 3.0 |
|
|
Dissipation factor | 100 Hz | 10-4 | IEC 60250 | 25 |
|
|
Dissipation factor | 1 MHz | 10-4 | IEC 60250 | 90 |
|
|
Volume resistivity | Ohm·m | IEC 60093 | 1E14 | |
|
|
Surface resistivity | Ohm | IEC 60093 | 1E16 | |
|
|
Electrical strength | 1 mm | kV/mm | IEC 60243-1 | 35 |
|
|
Comparative tracking index CTI | Solution A | Rating | IEC 60112 | 200 |
| Other properties (23 °C) | |||||
|
|
Water absorption (saturation value) | Water at 23 °C | % | ISO 62 | 0.4 |
|
|
Water absorption (equilibrium value) | 23 °C; 50 % r. h. | % | ISO 62 | 0.2 |
|
|
Density | kg/m3 | ISO 1183-1 | 1220 | |
| Glass fiber content | Method A | % | b.o. ISO 3451-1 | 10 | |
| Processing conditions for test specimens | |||||
|
|
Injection molding-Melt temperature | °C | ISO 294 | 260 | |
|
|
Injection molding-Mold temperature | °C | ISO 294 | 80 | |
|
|
Injection molding-Injection velocity | mm/s | ISO 294 | 540 | |
Disclaimer