苏州Bayblend FR3015 无锑无溴，无氯阻燃_FR3015

Bayblend FR3015
PC/ABS
无锑无溴，无氯阻燃;

注塑级，维卡/ B 120 = 118°C; UL 94 V-0（1.5毫米）;锑，氯和溴的阻燃剂。

[Datasheet Bayblend FR3015]

Property		Test Condition	Unit	Standard	typical Value
Rheological properties
	Melt volume-flow rate	260 °C; 5 kg	cm3/10 min	ISO 1133	20
	Molding shrinkage, parallel	150x105x3 mm	%	b.o. ISO 2577	0.5 - 0.7
	Molding shrinkage, normal	150x105x3 mm	%	b.o. ISO 2577	0.5 - 0.7
	Melt viscosity	1000 s^-1; 260 °C	Pa·s	b.o. ISO 11443-A	330
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	2700
	Yield stress	50 mm/min	MPa	ISO 527-1,-2	60
	Yield strain	50 mm/min	%	ISO 527-1,-2	4.5
	Stress at break	50 mm/min	MPa	ISO 527-1,-2	50
	Strain at break	50 mm/min	%	b.o. ISO 527-1,-2	> 50
	Izod impact strength	23 °C	kJ/m2	ISO 180-U	N
	Izod notched impact strength	23 °C	kJ/m2	ISO 180-A	35
Thermal properties
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	99
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	110
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	119
	Burning behavior UL 94 (1.5 mm) [UL recognition]		Class	UL 94	V-0
	Burning behavior UL 94-5V [UL recognition]	2.0 mm	Class	UL 94	5VB
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	960
Electrical properties (23 °C/50 % r. h.)
	Surface resistivity		Ohm	IEC 60093	1E16
Other properties (23 °C)
	Density		kg/m3	ISO 1183-1	1190
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	260
	Injection molding-Mold temperature		°C	ISO 294	80
	Injection molding-Injection velocity		mm/s	ISO 294	240