苏州Bayblend FR3005 无溴阻燃_无溴阻燃_东莞市大田化工有限公司

Bayblend FR3005 BBS310
PC/ABS
锑免费，无溴，氯，阻燃.

注塑级，维卡/乙120温度= 92°C，UL认可94 V-0（1.5毫米），锑，氯和无溴阻燃;改善的耐化学性。

[Datasheet Bayblend FR3005 BBS310]

Property		Test Condition	Unit	Standard	typical Value
Rheological properties
	Melt volume-flow rate	240 °C; 5 kg	cm3/10 min	ISO 1133	25
	Molding shrinkage, parallel	150x105x3 mm; 240 °C / MT 80 °C	%	b.o. ISO 2577	0.5 - 0.7
	Molding shrinkage, normal	150x105x3 mm; 240 °C / MT 80 °C	%	b.o. ISO 2577	0.5 - 0.7
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	2650
	Yield stress	50 mm/min	MPa	ISO 527-1,-2	60
	Yield strain	50 mm/min	%	ISO 527-1,-2	3.6
	Stress at break	50 mm/min	MPa	ISO 527-1,-2	45
	Strain at break	50 mm/min	%	b.o. ISO 527-1,-2	29
	Izod notched impact strength	23 °C	kJ/m2	ISO 180-A	14
	Charpy impact strength	23 °C	kJ/m2	ISO 179-1eU	N
Thermal properties
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	76
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	85
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	92
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10^-4/K	ISO 11359-1,-2	0.76
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10^-4/K	ISO 11359-1,-2	0.8
	Burning behavior UL 94 (1.5 mm)	1.5 mm	Class	UL 94	V-0
	Burning behavior UL 94-5V	1.5 mm	Class	UL 94	5VB
Other properties (23 °C)
	Water absorption (saturation value)	Water at 23 °C	%	ISO 62	0.5
	Water absorption (equilibrium value)	23 °C; 50 % r. h.	%	ISO 62	0.2
	Density		kg/m3	ISO 1183-1	1180
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	240
	Injection molding-Mold temperature		°C	ISO 294	80
	Injection molding-Injection velocity		mm/s	ISO 294	240

Disclaimer