供应JIS Z 8901 试验粉尘
JIS  Z  8901  试验粉尘  灰  灰尘  灰尘  

JIS粉尘是依据  JIS（Japanese  Industrial  Standard，即日本工业标准）生产的试验粉尘，常被用于一些日系产品的检测。
本公司可为广大国内用户提供日本进口的下述检测杂质，包括JIS  Z  8901的试验粉尘和玻璃珠产品；请在与我们联系的时候描述清楚您需要的是下面哪种产品：

JIS  Z  8901  
*Classification
Class    Material  used    Median  *
diameter
(  µm  )    Particle
density
(  g/cm3  )      Chemical  comPOSTTTION
%  (  mass  )
Class  1
Class  2
Class  3    Quartz  sand      185  to  200
27  to  31
6.6  to  8.6    2.6  to  2.7    SiO2        95min
Fe2O3,  Al2O3,TiO2
MgO,Ign.loss      
5max

Class  4
Class  9    Talc    7.2  to  9.2
4.0  to  5.0    2.7  to  2.9    SiO2  ???  60  to  63,    Al2O3  ???  0  to  3,    MgO  ???  30  to  34
Fe2O3  ???  0  to  3,    CaO  ???  0  to  2,    Ign.loss  ???  3  to  7

Class  5
Class  10    Fly  ash    13  to  17
4.8  to  5.7    1.95  min    SiO2Åc45min
Ign.lossÅc5max
Class  7
Class  8
Class  11    **
KANTO  
(Japanese)  loam    27  to  31
6.6  to  8.6
1.6  to  2.3    2.9  to  3.1    SiO2  ???  34  to  40,    Al2O3  ???  26  to  32,    MgO  ???  0  to  7
Fe2O3  ???  17  to  23,    CaO  ???  0  to  3,    Ign.loss  ???  0  to  4

Class  12      Carbon  black    Particle  size  range  ???  0.03  to  0.20  µm
Absorbed  amount  of  DBP  ???  25  to  34  ml/100g
Adsorbed  amount  of  iodine  ???  22  to  30  mg/g
Class  16
Class  17    Calcium-  
carbonate  (heavy)    3.6  to  4.6
1.9  to  2.4    2.7  to  2.8    CaO  ???  54  to  56,    SiO2  ???  0  to  3,    Ign.loss  ???  42  to  45
MgO  ???  0  to  3,    Fe2O3  ???  0  to  1    

*    Particle  size  distributions  are  defined  by  JIS  Z  8901.
**    Sintered  at  800°C,  2hours.
Note  :1)      Class15  Mixed  powder  is  distributed  by  Japan  Air  Cleaning  Association  and  contains  72%  of  Class8,  23%  of  Class12  and  5%  of  cotton  linter.
2)    Class13  and  Class  14  are  now  absent  ones.


*Particle  size  distribution  of  Test  Powders  1  
Particle  size  distribution  of
Class  1,  Class  2  and  Class  3
(  Quartz  sand  )
Particle
size  µm    Oversize(on  mass  basis)%
    Class  1    Class  2    Class  3
5    -    88±5    61±3
10    -    76±3    43±3
20    -    62±3    27±3
30    -    50±3    15±3
40    -    39±3    9±3
45    99  min.    -    -
75    90±3    20max.    3max.
106    80±3    -    -
150    65±3    -    -
212    45±3    -    -
300    1max.    -    -
      
Particle  size  distribution  of  
Class  4  and  Class  9
(  Talc  )
Particle
size  µm    Oversize(on  mass  basis)%
    Class  4    Class  9
2    -    79±5
4    -    55±5
5    69±5    -
8    -    23±5
10    40±5    -
16    -    6±3
20    12±5    -
30    -    -
40    3±3    -
75    1max    -


Particle  size  distribution  of
Class  5  and  Class  10
(  Fly  ash  )
Particle
size  µm    Oversize(on  mass  basis)%
    Class  5    Class  10
2    -    82±5
4    -    60±3
5    84±5    -
8    -    22±5
10    60±5    -
16    -    3±3
20    32±5    -
30    15±3    -
40    8±3    -
106    1max.      -
      
Particle  size  distribution  of
Class  7,  Class  8  and  Class  11
(  KNATO(Japanese)  loam  )
Particle
size  µm    Oversize(on  mass  basis)%
    Class  7    Class  8    Class  11
1    -    -    65±3
2    -    -    50±5
4    -    -    22±3
5    88±5    61±5    -
6    -    -    8±3
5    -    -    3±3
10    76±3    43±3    -
20    62±3    27±3    -
30    50±3    15±3    -
40    39±3    9±3    -
75    20max.      3max.      -

  
Class  12  Particle  size  range
(  Carbon  black  )
0.03~0.20µm  
      
Particle  size  distribution  of  
Class  16  and  Class  17
(  Calcium  carbonate(  heavy  ))
Particle
size  µm    Oversize(on  mass  basis)%
    Class  16    Class  17
1    -    80±5
2    76±5    54±5
4    -    18±5
5    40±5    -
8    -    4±3
10    10±5    -
16    -    1max.  
20    1max.      -


-=-=-=-=-=-=-=-=-=-=-=-=-=-=-=-=-
Glass  beads  GBL  type
Material  used  :  Soda  lime-silicate  glass  
Particle  density  :  2.1  to  2.5  g/cm3
Refractive  index  :  1.51  to  1.53  
Particle  size  distribution    (  Unit  :µm  )  (  %  mass  basis  )  
Class    Particle  size  in
case  of  90%  oversize      Particle  size  in
case  of  50%  oversize      Particle  size  in
case  of  10%  oversize  
GBL-30    26  min.    30  ±  1.0    34  max.
GBL-40    37  min.    40  ±  1.0    45  max.
GBL-60    55  min.    59  ±  1.0    63  max.
GBL-100    95  min.    100  ±  1.0    105  max.
  

Glass  beads  GBM  type
Material  used  :  Barium-titanate  glass  
Particle  density  :  4.0  to  4.2  g/cm3
Refractive  index  :  1.92  to  1.94  
Particle  size  distribution    (  Unit  :µm  )  (  %  mass  basis  )  
Class    Particle  size  in
case  of  90%  oversize      Parti