C
|
Mn
|
|
S
|
Si
|
Ni
|
Cr
|
Mo
|
≤0.24
|
0.7-1.6
|
≤0.035
|
≤0.035
|
0.15-0.5
|
≤0.25
|
≤0.25
|
≤0.08
|
机械性能
|
|
|
|
|
级别
|
钢板状态
|
屈服强度σ0.2(MPa)
|
抗拉强度σb(MPa)
|
延伸率δ4%
|
CL.1
|
正火
|
≥345
|
485-620
|
22
|
CL.2
|
淬火+回火
|
≥415
|
550-690
|
22
|
CL.3
|
淬火+回火
|
≥380
|
550-690
|
22
|
级别
|
钢板状态
|
板厚( mm )
|
最低冲击试验温度(℃)
|
Akv (纵向)( J )
|
CL.1
|
正火
|
≤ 25
|
-62
|
≥20
|
|
|
25-65
|
-60
|
|
|
|
65-75
|
-60
|
≥18
|
|
|
75-100
|
-46
|
|
CL.2
|
淬火+回火
|
≤ 65
|
-68
|
≥27
|
|
|
65-7575-100
|
-106
|
≥20
|