| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 |
1.1 - | ASTM D792 |
|
熔体体积流动速率(MVR) |
|||
280°C/5.0 kg |
7 cm3/10 min | ISO 1133 |
|
熔体质量流动速率(MFR) |
|||
280°C/5.0 kg |
7.4 g/10 min | ASTM D 1238 |
|
收缩率 |
|||
纵向(Flow) |
0.5~0.7 % | Internal |
flow, 3.2 mm |
横向(Across Flow) |
0.5~0.7 % | Internal |
on Tensile Bar, xflow |
吸水率 |
0.06 % | ASTM D570 |
23°C/Saturated |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 |
|||
屈服(yld) |
74 Mpa | ASTM D638 |
Type I, 50 mm/min |
屈服(yld) |
75 Mpa | ISO 527 |
|
断裂(brk) |
66 Mpa | ISO 527 |
|
断裂(brk) |
73 Mpa | ASTM D638 |
Type I, 50 mm/min |
拉伸延伸率 |
|||
屈服(yld) |
5.3 % | ASTM D638 |
Type I, 50 mm/min |
屈服(yld) |
5.2 % | ISO 527 |
|
断裂(brk) |
7.6 % | ASTM D638 |
Type I, 50 mm/min |
断裂(brk) |
13 % | ISO 527 |
|
弯曲强度 |
|||
屈服(yld) |
110 Mpa | ASTM D790 |
1.3 mm/min, 50 mm span |
屈服(yld) |
110 Mpa | ASTM D790 |
2.6 mm/min, 100 mm span |
- |
112 Mpa | ISO 178 |
|
弯曲模量 |
2650 Mpa | ASTM D790 |
1.3 mm/min, 50 mm span |
弯曲模量 |
2500 Mpa | ASTM D790 |
2.6 mm/min, 100 mm span |
弯曲模量 |
2520 Mpa | ISO 178 |
|
拉伸模量 |
2380 Mpa | ASTM D638 |
5 mm/min |
拉伸模量 |
2220 Mpa | ISO 527 |
1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) |
|||
-30℃ (-22℉) |
55 J/m | ASTM D256 |
|
23℃ (73℉) |
190 J/m | ASTM D256 |
|
23℃ (73℉) |
15 kJ/m2 | ISO 180/1A |
80*10*4 |
仪器化落镖冲击能量 |
|||
23℃ (73℉)总能量 |
54 J | ASTM D3763 |
|
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R |
119 R | ASTM D785 |
|
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) |
|||
0.45 Mpa (66 psi)（4.6kg/cm2） |
155 °C | ASTM D648 |
3.2mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm2） |
156 °C | ISO 75/Be |
Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm2） |
140 °C | ASTM D648 |
3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） |
145 °C | ASTM D648 |
6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） |
140 °C | ISO 75/Ae |
Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) |
164 °C | ISO 306 |
Rate B/120 |
维卡软化温度(Vicat) |
162 °C | ISO 306 |
Rate B/50 |
相对温度指数(RTI) |
|||
冲击w/impact,- |
105 °C | UL 746B |
|
电气Elec,- |
105 °C | UL 746B |
|
强度w/o impact,- |
105 °C | UL 746B |
|
线性膨胀系数(CLTE) |
|||
纵向(Flow) |
80 E-6/°C | ASTM E831 |
-40°C to 40°C, flow |
横向(Across Flow) |
80 E-6/°C | ASTM E831 |
-40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 |
|||
V-0 |
1.5 mm | UL94 |
Min. |
5VA |
2 mm | UL94 |
Min. |
灼热丝可燃性指数(GWFI) |
|||
1.5mm |
960 °C | IEC 60695-2-12 |
|
2mm |
960 °C | IEC 60695-2-12 |
|
3mm |
960 °C | IEC 60695-2-12 |
|
灼热丝点燃温度(GWIT) |
|||
1.0mm |
825 °C | IEC 60695-2-13 |
|
1.5mm |
825 °C | IEC 60695-2-13 |
|
2.0mm |
825 °C | IEC 60695-2-13 |
|
3.0mm |
800 °C | IEC 60695-2-13 |
|
PPO用途
1、适于制作耐热件、绝缘件、减磨耐磨件、传动件、医疗及电子零件。
2、可作较高温度下使用的齿轮、风叶、阀等零件，可代替不锈钢使用。
3、可制作螺丝、紧固件及连接件。
4、电机、转子、机壳、变压器的电器零件。
5、PPO和MPPO 主要用于电子电器、汽车、家用电器、办公室设备和工业机械等方面，利用MPPO耐热性、耐冲击性、尺寸稳定性、耐擦伤、耐剥落。
6、可涂性和电气性能，用于做汽车仪表板、散热器格子、扬声器格栅、控制台、保险盒、继电器箱、连接器、轮罩。
7、电子电器工业上广泛用于制造连接器、线圈绕线轴、机械部件护罩、开关继电器、调谐设备、大型电子显示器、可变电容器、蓄电池配件、话筒等零部件。
8、家用电器上用于电视机、摄影机、录象带、录音机、空调机、加温器、电饭煲等零部件。可作复印机、计算机系统，打印机、传真机等外装件和组件。
9、另外可做照相机、计时器、水泵、鼓风机的外壳和零部件、无声齿轮、管道、阀体、等零部件。