| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
简支梁缺口(Charpy Notched) |
|||
23℃ (73℉) |
15 kJ/m2 | ISO 179/1eA |
V-notch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) |
|||
-30℃ (-22℉) |
144 J/m | ASTM D256 |
|
-30℃ (-22℉) |
10 kJ/m2 | ISO 180/1A |
80*10*4 |
23℃ (73℉) |
192 J/m | ASTM D256 |
|
23℃ (73℉) |
16 kJ/m2 | ISO 180/1A |
80*10*4 |
仪器化落镖冲击能量 |
|||
23℃ (73℉)总能量 |
47 J | ASTM D3763 |
|
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) |
|||
1.8 Mpa (264 psi)（18.6kg/cm2） |
140 °C | ASTM D648 |
3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） |
141 °C | ISO 75/Af |
Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) |
161 °C | ASTM D1525 |
Rate B/50 |
维卡软化温度(Vicat) |
162 °C | ISO 306 |
Rate B/120 |
维卡软化温度(Vicat) |
160 °C | ISO 306 |
Rate B/50 |
线性膨胀系数(CLTE) |
|||
纵向(Flow) |
70.9 E-6/°C | ASTM E831 |
-40°C to 40°C, flow |
纵向(Flow) |
70.9 E-6/°C | ISO 11359-2 |
-40°C to 40°C, flow |
横向(Across Flow) |
68.7 E-6/°C | ASTM E831 |
-40°C to 40°C, xflow |
横向(Across Flow) |
68.7 E-6/°C | ISO 11359-2 |
-40°C to |