| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
|
|||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
特性
|
|
|||
|
机构评级
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.27
|
g/cm3
|
ASTM D792, ISO 1183 |
|
熔流率 (337°C/6.6
kg)
|
18
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR） (340°C/5.0
kg)
|
13.0
|
cm3/10min
|
ISO 1133 |
|
收缩率 - 流动 (3.20 mm)
|
0.50 到 0.70
|
%
|
内部方法 |
|
吸水率
|
|||
|
24
hr
|
0.25
|
%
|
ASTM D570 |
|
饱和,
23°C
|
1.3
|
%
|
ISO 62 |
|
平衡,
23°C
|
1.3
|
%
|
ASTM D570 |
|
平衡, 23°C,
50% RH
|
0.70
|
%
|
ISO 62 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度 (M 计秤)
|
109
|
|
ASTM D785 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 2
|
3590
|
MPa
|
ASTM D638 |
|
--
|
3200
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服 3
|
110
|
MPa
|
ASTM D638 |
|
屈服
|
105
|
MPa
|
ISO 527-2/5 |
|
断裂 3
|
110
|
MPa
|
ASTM D638 |
|
断裂
|
85.0
|
MPa
|
ISO 527-2/5 |
|
伸长率
|
|||
|
屈服 3
|
7.0
|
%
|
ASTM D638 |
|
屈服
|
6.0
|
%
|
ISO 527-2/5 |
|
断裂 3
|
60
|
%
|
ASTM D638 |
|
断裂
|
60
|
%
|
ISO 527-2/5 |
|
弯曲模量
|
|||
|
50.0
mm 跨距 4
|
3500
|
MPa
|
ASTM D790 |
|
-- 5
|
3300
|
MPa
|
ISO 178 |
|
弯曲强度
|
|||
|
-- 5, 6
|
160
|
MPa
|
ISO 178 |
|
屈服,
100 mm 跨距 7
|
165
|
MPa
|
ASTM D790 |
|
抗泰伯磨耗 (1000 Cycles, 1000 g, CS-17
转轮)
|
10.0
|
mg
|
ASTM D1044 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度 8 (23°C)
|
5.0
|
kJ/m2
|
ISO 179/1eA |
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
30
|
J/m
|
ASTM D256 |
|
23°C
|
32
|
J/m
|
ASTM D256 |
|
-30°C 9
|
无断裂
|
|
ISO 180/1A |
|
23°C 9
|
无断裂
|
|
ISO 180/1A |
|
无缺口悬臂梁冲击 (23°C)
|
1300
|
J/m
|
ASTM D4812 |
|
反向缺口冲击 (3.20 mm)
|
1200
|
J/m
|
ASTM D256 |
|
装有测量仪表的落镖冲击 (23°C, Total
Energy)
|
38.0
|
J
|
ASTM D3763 |
|
落锤冲击 (23°C)
|
33.9
|
J
|
ASTM D3029 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度
|
|||
|
0.45 MPa,
未退火, 6.40 mm
|
207
|
°C
|
ASTM D648 |
|
1.8 MPa,
未退火, 3.20 mm
|
190
|
°C
|
ASTM D648 |
|
1.8 MPa,
未退火, 6.40 mm
|
198
|
°C
|
ASTM D648 |
|
1.8
MPa, 未退火, 64.0 mm 跨距 10
|
190
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
211
|
°C
|
ASTM D1525 11, ISO 306/B50 11 |
|
--
|
212
|
°C
|
ISO 306/B120 |
|
Ball Pressure
Test (75°C)
|
Pass
|
|
IEC 60695-10-2 |
|
线形膨胀系数
|
|||
|
流动 : -20 到
150°C
|
5.5E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : -40 到
40°C
|
5.5E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
横向 : -40 到
40°C
|
5.5E-5
|
cm/cm/°C
|
ASTM E831, ISO 11359-2 |
|
导热系数
|
0.22
|
W/m/K
|
ASTM C177 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
1.0E+17
|
ohm·cm
|
ASTM D257 |
|
介电强度
|
ASTM D149 | ||
|
1.60 mm, in
Air
|
33
|
kV/mm
|
|
|
1.60 mm, in
Oil
|
28
|
kV/mm
|
|
|
介电常数 (1 kHz)
|
3.15
|
|
ASTM D150 |
|
耗散因数
|
ASTM D150 | ||
|
1
kHz
|
1.3E-3
|
|
|
|
2.45
GHz
|
2.5E-3
|
|
|
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
极限氧指数
|
44
|
%
|
ASTM D2863 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
149
|
°C
|
|
|
干燥时间
|
4.0 到 6.0
|
hr
|
|
|
干燥时间，最大
|
24
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注入量
|
40 到 60
|
%
|
|
|
螺筒后部温度
|
332 到 399
|
°C
|
|
|
螺筒中部温度
|
338 到 399
|
°C
|
|
|
螺筒前部温度
|
343 到 399
|
°C
|
|
|
射嘴温度
|
343 到 399
|
°C
|
|
|
加工（熔体）温度
|
349 到 399
|
°C
|
|
|
模具温度
|
135 到 163
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|