3M Scotchcast #8N电气绝缘树脂3M? Scotchcast? Electrical Resin 8N
3M Scotchcas 环氧树脂 8N 套装 (组分A和组分B)
3M Scotchcast Electrical Resin 8N is a low-stress, highly moisture-resistant compound that cures at room temperature. This epoxy resin system offers long pot life,
low viscosity, a 1:1 mix ratio (by weight), Class B (130C) temperature rating, and is commonly used to coat printed circuit boards, pot connectors, and impregnate electrical and electronic components. Because of its low exotherm, Scotchcast resin 8 is also frequently specified for impregnating and encapsulating temperature sensitive units.
.Low exotherm
. High moisture resistance
. Highly resistant to mechanical and thermal shock
. Extended pot life
a、特点
3M Scotchcast 8N 电气绝缘双组分环氧树脂为未填充树脂，该产品的特点是半柔软、耐潮性、低放热、机械性能稳定性以及优越的耐热冲击性能。该型号树脂具有极长的使用有效期，且粘度较低。重量混合比为1：1，可以室温固化，为获得性能，建议适当延长固化时间。
b、应用范围
该树脂被广泛用于PCB板、连接器及其他电气电子组件的灌注、密封及包涂。鉴于该树脂固化时的低放热性，#8树脂经常地被用于温度元件的灌注。
· 低放热性
· 优良的耐潮性
· 优良的机械性能及耐热冲击性
· 长期的使用有效期
c、使用信息
（1）混合
先将两组分分别混合，加温到60℃会有助于混合(该产品的凝胶时间大约为30min@60℃)。称取正确比例的两组分，并充分混合，直至颜色完全一致，或者直到混合物完全均匀。
（2）除气
为除去混合时产生的气体，可以在5-10mmHg的压力下抽气，加温有助于除气，容器壁高度应有液态树脂高度的四倍，以便容纳泡沫。
（3）灌注和注入
灌注温热的树脂到已经预热到100℃的模具中。如果不采用模具，可以将预热了的组件浸在树脂中。加热树脂、组件以及模具以帮助注入。为的注满，可以在5mmHg的压力下抽气，或者真空下灌注并维持几分钟再开模。
（4）固化
如果考虑到***小应力和的热冲击性，推荐采用环境温度固化程序。如果需要采用烤箱固化，建议给予一段升温时间，以使温度从室温到固化温度。固化程序具体可以参照操作性能。如果固化温度不能太高，且所需固化的树脂面积不是很大，该树脂可以在95℃下1h快速固化。
（5）储存
该树脂体系具有至少一年的储存期。两种组分都应储存在干燥通风的区域，不使用时应将容器扎紧密封。
d、操作及安全注意事项
在使用本产品前，请仔细阅读在产品安全书(MSDS)和/或化学品标签上的健康危害警告和应急处理方法等内容。